An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Reine Metalle • r sinkt linear mit T • bei T0:   konstant Matthiessen Theorie

  2. Legierungen Matthiesen  die Steigung in der Abhängigkeit R vs. T bleibt konstant

  3. Fremde Atome und Versetzungen Molybdän D. Rafaja, H. Köstenbauer, U. Mühle, C. Löffler, G. Schreiber, M. Kathrein, J. Winkler: Effect of the deposition process and substrate temperature on the microstructure defects and electrical conductivity of molybdenum thin films, Thin Solid Films 528 (2013) 42-48.

  4. Atomare Anordnung

  5. Atomare Anordnung in Au-Cu Au-Cu, Fm3m Au3Cu, Pm3m AuCu, P4/mmm AuCu3, Pm3m Röntgenbeugung - zusätzliche Beugungslinien

  6. Elektrische Leitfähigkeit von Er(Co1-xGex)2 S. Daniš, P. Javorský, D. Rafaja and V. Sechovský: Low-temperature transport and crystallographic studies of Er(Co1-xSix)2 and Er(Co1-xGex)2, J. Alloys Comp. 345 (2002) 54-58.

  7. Gitterparameter von Er(Co1-xSix)2 • ErCo2 • kubische Struktur (Fd3m) • rhombische Verzerrung • magnetische Anordnung • Änderung des Widerstandes 33 K S. Daniš, P. Javorský, D. Rafaja and V. Sechovský: Low-temperature transport and crystallographic studies of Er(Co1-xSix)2 and Er(Co1-xGex)2, J. Alloys Comp. 345 (2002) 54-58.

  8. Kristallstruktur von ErCo2 Richtung {111} Co Er ErCo2, SG: Fd3m Er (8a): (0,0,0) Co (16d): (5/8, 5/8, 5/8)

  9. Kondo-Effekt Abweichung von der Matthiesenschen Regel Spin-Beitrag: Phononen Spin Spezifischer Widerstand, mWcm Legierungen: Cu, Ag, Au, Mn, Zn dotiert mit: Cr, Mn, Fe J. Kondo: Prog. Theor. Phys. 32 (1964) 37.