1 / 7

FRATTOGRAFIA

FRATTOGRAFIA. Tipi di frattura fragile duttile a fatica per creep Prove di frattura. Obiettivo : strumenti per determinare le cause della rottura di un materiale. Teoria di Griffith c = 10 -4 m r = 10 -10 m S c = 10 3 S. Frattura FRAGILE. Tre stadi

adrienne-roderick
Download Presentation

FRATTOGRAFIA

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. FRATTOGRAFIA • Tipi di frattura • fragile • duttile • a fatica • per creep • Prove di frattura Obiettivo: strumenti per determinare le cause della rottura di un materiale

  2. Teoria di Griffith c = 10-4 m r = 10-10 m Sc = 103 S Frattura FRAGILE

  3. Tre stadi 1) concentrazione delle dislocazioni (durante il regime plastico) 2) formazione di microcricche dove sono concentrate le dislocazioni 3) propagazione delle microcricche e frattura Frattura intergranulare Avanza lungo i bordi di grano • Frattura intragranulare • Avanza lungo piani cristallografici caratteristici detti piani di clivaggio • fcc (111) • bcc(100)

  4. Tre stadi 1) formazione di microcricche 2) coalescenza delle microcricche (90°) 3) incrudimento del materiale e evento finale di frattura (45°) Frattura DUTTILE