An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Why Study Corrosion 1 Sheldon W. Dean 12/7/02

  2. What is Corrosion? What does it look like? How do you know when you have it?

  3. What is Corrosion? • Metals made by smelting ( reduction of ore) • Metals in air want to return to their oxidized state • Corrosion is a natural process!

  4. Is Corrosion Important? • National issue? • International issue? • What industries are affected? • Does it affect us personally?

  5. Importance to USA • CC Technologies study – March 2002 • In 2000 about 3.1% of GDP spent on corrosion repair and control • Total cost $276Billion! • Of industries analyzed, the cost was $137.9 Billion

  6. Examples of Corrosion Damage • Automotive problems - body rust • Home examples- - Plumbing fixtures - Mail box - Exterior fixtures and fasteners • Concrete cracking

  7. Corrosion Affects Our Safety! • Unexpected failures of equipment and devices • Need to replace damaged items • Corrosion weakens structures - Need to evaluate fitness for service when corrosion occurs

  8. What Does Corrosion Look Like? • Rust and tarnish, red blue or gray scale • 8 types of damage – Fontana • Several others also.

  9. Most Common Forms of Corrosion • General attack (uniform wastage) • Pitting/ Crevice attack • Cracking (embrittlement) • Galvanic corrosion

  10. Corrosion is Electrochemical • Two different reactions occur - oxidation and reduction • Electron transfer occurs • Potential (voltage) driving force required • Oxidation occurs at anode • Reduction occurs at cathode

  11. Corrosion Reactions • Oxidation - e.g. Fe  Fe++ + 2e • Reduction – e.g. O2 + 2H2O  4OH- - 4e • Secondary - e.g. 4 Fe++ + O2  Fe2O3 + 8H+

  12. Conclusions • Corrosion rate depends upon the corrosion products that form • Solubility of corrosion products determines the rate • If solubility is high, the rate is high! • If solubility is low, the rate is low

  13. Potential/pH (Pourbaix) Diagram • Very useful way to present data • Developed by Marcel Pourbaix (1966) • Available for all metals and many other elements • Shows solubility and potential effects • If solubility is < 10-6 M/l, no corrosion is assumed

  14. Characteristics of Corrosion Products • Very thin and dense: protective,e.g., Cr, Al, Ti, 10 to 100 nm thick • Thin: protective but some corrosion occurs, e.g.,Cu, Zn, Pb 1 to 10 m • Thick and porous, e.g., Fe, >100 m Corrosion is a problem. • Soluble, e.g., Na, K Not able to be used.

  15. Dealing with Corrosion There are many ways to prevent or minimize corrosion damage

  16. Alloying to Resist Corrosion - Steel • Add >13% Cr (stainless steel) • Add >2% Mo to stainless (to resist pitting) • Add Si, P, Cu, Cr ( and others) to obtain weathering steel

  17. Alloying to Resist Corrosion - Copper • Add Ni and Fe (cupronickel) sea water • Add As, Sb, or P to prevent dealloying of brass (Cu + 10 to 35% Zn) • Add Al or Si to resist erosion

  18. Metallic Coatings • Widely used to protect steel and to make other metals more attractive • Zn and Zn alloys on steel – Galvanizing • Ni + Cr on steel, brass or zinc to give a bright finish • Cu + Ni + Cr also used for bright finish

  19. Organic Coatings - Paint • Barrier layer to keep water away • Adhesion is key to success • Susceptible to thermal damage • Susceptible to UV damage

  20. Electrochemical Protection • Cathodic protection – reduce the potential and also corrosion rate - widely used underground and in sea water • Anodic protection – increase potential to produce a less soluble corrosion product – used in some chemical plants

  21. Corrosion Inhibitors • Used in water systems: - Automotive cooling systems - Cooling towers - Boilers, especially high pressure steam • Temporary preservatives for metals - Volatile corrosion inhibitors • Paints and primers

  22. Quiz Time! • What is the most corrosive substance we can think of? • Corrosion damage only causes metals to become thinner – True or False? • How does corrosion affect me?

  23. Answers! • Water!!! • False! Corrosion also causes cracking, pitting, staining, wedging in crevices, loss of electrical conductivity, and failure of components • What is your answer?

  24. Break Time

  25. Why Study Corrosion - 2 Sheldon Dean 12/7/02

  26. Careers in CorrosionTechnician - Education • High school diploma + interest in chemistry or technology • Associates degree – possible night school - not required at entry level - Chemistry - Electrical technology - Materials science

  27. Careers in CorrosionTechnician-Work • Lab technician - Chemistry laboratory - Materials laboratory - Materials or chemical company • Field technician – civil engineering - Pipeline monitoring - Bridges, tunnels etc.

  28. Careers in CorrosionCivil Engineer - Education • Civil, mechanical or electrical SB • MBA or MS (not required but often helpful) • PE license • NACE Certification

  29. Careers in CorrosionCivil Engineer - Work • Engineering firm or consultant - Cathodic protection design - System monitoring and evaluation • State or local government - Specify protection systems for bridges, tunnels, other facilities - Inspection and monitoring

  30. Mat., Chem., Chem. Eng.Education • High School Diploma • College SB, Major: Mat. Eng., Chem., Chem. Eng., or Mech.Eng. • Grad school optional, MBA, MS or PhD • Certification NACE (optional) • PE License (optional)

  31. Mat.,Chem.,Chem. Eng.Work • Chemical, materials, petroleum, auto firm - Engineering - Safety - Research (PhD) - Plant Maintenance • Engineering or consultant firm

  32. NACE International • Short courses, some with certification • Annual meeting and show • Standards development • Local sections • Symposia • Books, videos and computer products

  33. NACE InternationalThe Corrosion Society • Address: P.O.Box218340, Houston,TX77218-8340 • Phone: 281-228-6200 • Website: www.nace.org

  34. ASTM International • Standards development, Vol.03.02 • Training courses • Symposia • Address:100 Barr Harbor Drive, West Conshocken, PA 19428-2959 • Website: www.astm.org • Corrosion committee: G-1

  35. Corrosion Testing • Used for a variety of purposes • Standard test methods available • Some tests are simple and easy to run • ASTM corrosion tests are in Volume 03.02 of the “Annual Book of ASTM Standards”

  36. Corrosion Testing-Purposes • Accelerated tests to demonstrate products durability • Acceptance tests to show that a material meets standard • Monitoring tests to show changes in a system corrosivity • Research tests to determine mechanism of corrosion

  37. Standard Tests • Usually corrosion tests have many parameters • Corrosion tests often give results that are difficult to reproduce – Standardization helps reproducibility • Consensus standard tests: ASTM and NACE

  38. Accelerated Test Example • ASTM G48 Pitting and Crevice Corrosion Resistance • Ferric chloride, 6%solution • 72Hrs at 22oC (room temperature) • Report pitting or crevice corrosion • Simulates sea water attack of stainless steels

  39. Acceptance Test - Al Alloys • ASTM G 69, Test of metallurgical condition of Al alloys • Measure potential,E, in salt solution • Cu increases E, Zn reduces E • Heat treatment determines condition • Condition affects strength and corrosion tendencies

  40. ASTM G 69 Continued • Solution: 1M Na Cl + 2.7%H2O2, 22oC • Surface preparation: 00 steel wool rub • 1 Hour immersion • Measure potential every 5 minutes after 30 minutes against SCE electrode • Average result: -750+/-10mV for pure Al • Al foil is pure Al