Impact of Potassium Acetate Deicing Chemicals on ASR of Candidate OMP Concrete Materials. Francis B. Nelson III Leslie J. Struble January 12, 2006. Overview. Alkali Silica Reaction Previous Work Deicer Background Tasks Schedule Testing Programs. Alkali Silica Reaction.

loader
I am the owner, or an agent authorized to act on behalf of the owner, of the copyrighted work described.
capcha
Download Presentation

PowerPoint Slideshow about 'Impact of Potassium Acetate Deicing Chemicals on ASR of Candidate OMP Concrete Materials' - yvon


An Image/Link below is provided (as is) to download presentation

Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author.While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server.


- - - - - - - - - - - - - - - - - - - - - - - - - - E N D - - - - - - - - - - - - - - - - - - - - - - - - - -
Presentation Transcript
Impact of potassium acetate deicing chemicals on asr of candidate omp concrete materials l.jpg

Impact of Potassium Acetate Deicing Chemicals on ASR of Candidate OMP Concrete Materials

Francis B. Nelson III

Leslie J. Struble

January 12, 2006


Overview l.jpg
Overview Candidate OMP Concrete Materials

  • Alkali Silica Reaction

  • Previous Work

  • Deicer Background

  • Tasks

  • Schedule

  • Testing Programs


Alkali silica reaction l.jpg
Alkali Silica Reaction Candidate OMP Concrete Materials

  • Chemical reaction between alkali and hydroxide ions in pore solution and reactive silica in aggregate

  • Reaction produces gel

  • Gel adsorbs water and swells, causing expansion and cracking of aggregate


Affected concretes l.jpg
Affected Concretes Candidate OMP Concrete Materials

Highway pavement and bridge abutment in Peoria, Illinois

Concrete anchor for cable-stay bridge, Royal Gorge, Colorado


Effect of supplemental cementing materials l.jpg
Effect of Supplemental Cementing Materials Candidate OMP Concrete Materials

  • Fly ash, slag, silica fume, metakaolin all reduce expansion by replacing cement, lowering alkali concentration

  • Effective replacement level must be determined for specific material

PCA


To prevent asr l.jpg
To Prevent ASR Candidate OMP Concrete Materials

  • Recognize and avoid susceptible aggregate

  • Use low alkali cement

  • Use supplemental cementing material


Previous work l.jpg
Previous Work Candidate OMP Concrete Materials

  • Tech Notes

  • IDOT work

  • UIUC Testing

  • Recommendations to OMP


Tech notes l.jpg
Tech Notes Candidate OMP Concrete Materials

  • #9 – Freeze Thaw Performance of Coarse Aggregates

    • Recommended Use of IDOT F/T list

  • #10 – Summary of IDOT & ASTM Specifications for Coarse Aggregate Gradation

    • Described CA Gradations for Use at OMP

  • #20 – FAA Concrete Materials Specification Evaluation

    • Recommended Material Guidelines for OMP


Idot working group meetings l.jpg
IDOT Working Group Meetings Candidate OMP Concrete Materials

  • Working with Industry to develop ASR specification

  • Slowly introduce a statewide specification (June 2006)

    • Special provision on job specific basis (Dan Ryan Project using GGBFS)

  • Only District 4 (Peoria) showing evidence in pavements of ASR currently

    • Other districts have reactive aggregates however

  • Developing List of Fine Aggregate Producers

    • Proposed Four Categories of Aggregate Reactivity

    • According to ASTM C 1260 Test Results

  • Allowing mitigation according to ASTM C 1567


Uiuc asr testing l.jpg
UIUC ASR Testing Candidate OMP Concrete Materials

  • Aggregates selected from Chicago market

    • 5 natural sands and 1 manufactured sand

    • Ottawa sand and Pyrex glass


Uiuc asr recommendations l.jpg
UIUC ASR Recommendations Candidate OMP Concrete Materials

  • Two categories of expansion rather than three (<0.1% and >0.1%)

  • No maximum alkali content for cements (due to potassium in deicer)

  • Allow contractors to use ASTM C 1567 to make a combination of aggregate, cement, and mineral admixture that yields expansion less than 0.1%


Mitigating asr testing l.jpg
Mitigating ASR Testing Candidate OMP Concrete Materials

  • Test Mineral Admixtures

    • Test for potential combinations to mitigate against reactive aggregates, use ASTM C 1567 test method.

    • Use fine aggregates previously tested and combine with mitigating materials, such as fly ash and slag, to test for decreased expansion.


Mitigating materials test program l.jpg
Mitigating Materials Test Program Candidate OMP Concrete Materials

  • ASTM C 1567

    • Class F Fly Ash

      • 15%, 10%, 5%, +/-

    • Class C Fly Ash

      • 15%, +/-

    • Ground Granulated Blast Furnace Slag

      • 20%, 25%, 15%, +/-

    • Silica Fume*

      • 10%, +/-

    • Metakaolin*

      • 10%, +/-


Background on potassium acetate deicer l.jpg
Background on Potassium Acetate Deicer Candidate OMP Concrete Materials

  • Non-chloride based deicer

  • Non-toxic, Biodegradable and less corrosive

  • Lowers freezing temperature (-76o F)

  • Also anti-icing agent (prevents freezing)

  • Avoid use with non air entrained concrete, galvanized metals, and non-watertight electrical systems


Tasks l.jpg
Tasks Candidate OMP Concrete Materials

  • Conduct literature review

  • Select representative fine aggregates

  • Survey/test deicing chemical

  • Test selected samples for ASR using ASTM C 1260 modified to simulate potassium acetate solution

  • Test mitigating materials for effective level of replacement according to ASTM C 1567

  • Obtain concrete cores from pavement using deicer

  • Examine cores for possible alkali-silica reaction

  • Recommend materials for OMP pavements

  • Write final report at end of project and Technical Notes as necessary throughout the study.


Schedule l.jpg
Schedule Candidate OMP Concrete Materials


Potassium acetate studies l.jpg
Potassium Acetate Studies Candidate OMP Concrete Materials

  • Modified ASTM C 1260 tests

    • Work done by Prasad Rangaraju, PhD

  • pH and Chemical Composition

Rangaraju et al 2005


Modified astm c 1260 l.jpg
Modified ASTM C 1260 Candidate OMP Concrete Materials

  • Compare 14 day expansions between NaOH (left) and PA (right)

Rangaraju et al 2005


Mortar bars and concentration l.jpg
Mortar Bars and Concentration Candidate OMP Concrete Materials

  • Concentration of 6.46 M is what is applied to pavements

  • Expansion accelerated so much tests ended due to severe cracking and warping of mortar bars

Rangaraju et al 2005


Deicer testing program l.jpg
Deicer Testing Program Candidate OMP Concrete Materials

  • 5 natural sands tested previously

    • Test in deicer solution and compare expansions

  • Test mitigating mixtures from ASTM C 1567 results

    • Test in deicer solution and compare expansions


Assistance from omp l.jpg
Assistance from OMP Candidate OMP Concrete Materials

  • Obtaining cores from pavements at Midway and/or O’Hare

  • History and understanding of deicer use so far in Chicago

  • Open for discussion