4.2. CAD Output Devices - Rapid Prototyping

ME 521 Computer Aided Design. 4.2. CAD Output Devices - Rapid Prototyping. Dr . Ahmet Zafer Şenalp e-mail: azsenalp@gyte.edu.tr Makine Mühendisliği Bölümü Gebze Yüksek Teknoloji Enstitüsü. 4.2. CAD Output Devices Rapid Prototyping. Rapid Prototyping.

xuxa
Download Presentation

4.2. CAD Output Devices - Rapid Prototyping

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. ME 521 ComputerAidedDesign 4.2. CAD OutputDevices-RapidPrototyping Dr. Ahmet Zafer Şenalpe-mail: azsenalp@gyte.edu.tr Makine Mühendisliği Bölümü Gebze Yüksek Teknoloji Enstitüsü

  2. 4.2. CAD OutputDevices RapidPrototyping RapidPrototyping • It is the technology that using CAD models physical models are obtained directly. For this purpose rapid prototyping devices are used. • Although rapid prototyping devices vary in its group their principles are the same. In this method physical models are formed by adding materials layer by layer. • Rapid Prototyping (RP) brings solutions to the problems faced during product development period. Possible design mistakes can easily be identified. • Before the mass production, prototype has to be prepared and several tests have to be conducted on these prototypes. This period may take a long time when conducted with conventional methods. With RP this period is shortened and prototypes can be tested both visually and functionally. • Possible design changes can be decided on these prototypes and necessary changes can easily be made. • Prototypes can be used for die manufacturing. GYTE-Makine Mühendisliği Bölümü

  3. 4.2. CAD OutputDevices RapidPrototyping RapidPrototyping Where are the parts produced by RP used? • After visual inspection possible shape mistakes can be identified. • For products that contain more than one part perfect assembly conditions (ex: alignment) can be checked. • Mechanism functionality can be tested. • An assembly with a lot of parts can be manufactured and run at one time. • Prototypes can be used for die manufacturing . • Prototype models can be used of precise casting. GYTE-Makine Mühendisliği Bölümü

  4. 4.2. CAD OutputDevices RapidPrototyping RapidPrototyping What kind of parts can be produced by RP? • There is even no limitation to the parts that can be produced by RP. As the parts can easily be bonded to each other, the size of the part is not a problem. • Die production can also be made with RP. GYTE-Makine Mühendisliği Bölümü

  5. 4.2. CAD OutputDevices RapidPrototyping RapidPrototyping How much time is needed for RP? Hours!... Time needed for RP depends on complexity and volume of the part. The delivery time is about 4-5 days after ordering. In special cases the period can be short as 1 day or long as 10 days. GYTE-Makine Mühendisliği Bölümü

  6. 4.2. CAD OutputDevices RapidPrototyping RapidPrototyping Is RP expensive?RP can be seen as expensive with the additional cost . However with RP the work that could be concluded in weeks can be finished in hours. Product defects can be detected earlier and much more expensive corrections can be avoided. With these advantages apparent cost for RP is less than the savings made by using RP. The RP cost of products depends on factors like product size, volume and geometry. Real cost of products should be determined after conducting necessary analysis. GYTE-Makine Mühendisliği Bölümü

  7. 4.2. CAD OutputDevices RapidPrototyping RapidPrototyping Rapid Prototyping Technologies: • Polyjet • FDM: Fused Deposition Modeling • SLS: Selective Laser Sintering • SLA: Stereolithography • LOM: Laminated Object Manufacturing • EBM: Electron Beam Melting • 3-D Printing GYTE-Makine Mühendisliği Bölümü

  8. 4.2. CAD OutputDevices RapidPrototyping Polyjet In this technique, photo-polymer material in liquid form at room temperature is sprayed from spray nozzles of eight injection heads with thousands of injection spray nozzles which cause the formation of layers (similar to plastic injection machines). The sprayed material is freezed and solidified by using ultraviolet lamps. 16 micron thickness layers are formed one by one and prototype is obtained. As the model can not stop hanging in the air, the gaps are filled with support material with the same injection method. This support material then dissolves in water and the model is obtained. The materials used in this technology are photo-polymer resins which are specific to this method. Physical and chemical properties differ from each other. GYTE-Makine Mühendisliği Bölümü

  9. 4.2. CAD OutputDevices RapidPrototyping Polyjet ...... STL file is opened in the software and model is placed on the system’s table and the file is send to the Polyjetfrom the software. Polyjet system sprays the model and support material according to the instructions send by the software. After each layer sprayed material is applied ultraviolet rays for solidification. Model is constructed in 16 micron thickness layers. Then water spay is used to remove support material from the model and prototype is obtained. GYTE-Makine Mühendisliği Bölümü

  10. 4.2. CAD OutputDevices RapidPrototyping Polyjet PolyjetMatrix GYTE-Makine Mühendisliği Bölümü

  11. 4.2. CAD OutputDevices RapidPrototyping Polyjet PolyjetProduct Examples: FullCure 720 Tango : TangoBlack & TangoGray GYTE-Makine Mühendisliği Bölümü

  12. 4.2. CAD OutputDevices RapidPrototyping Polyjet PolyjetProduct Examples: Tango plus Vero : VeroBlue, VeroWhite, VeroBlack GYTE-Makine Mühendisliği Bölümü

  13. 4.2. CAD OutputDevices RapidPrototyping FDM: FusedDepositionModeling Fused deposition modeling (FDM) is an additive manufacturing technology commonly used for modeling, prototyping, and production applications. The technology was developed by S. Scott Crump in the late 1980s and was commercialized in 1990. The FDM fused deposition model process is additive which extrudes material in layers. A plastic filament is melted and extruded through a heated nozzle. The nozzle moves to produce a profile of the part then moves down and the next layer is built on top until the entire prototype model is fully built. The model is complete and requires no hardening. FDM is an excellent choice for any 3D Model that needs to closely represent the final product in strength and durability. CAD Models can be produced in about 24 hours depending on the size and complexity. Online price quotes are available for FDM parts.. FDM requires support during the Prototype Model building process and can increase the build time. Several materials are available with different trade-offs between strength and temperature properties. As well as acrylonitrile butadiene styrene (ABS) polymer, polycarbonates, polycaprolactone, polyphenylsulfones and waxes. A "water-soluble" material can be used for making temporary supports while manufacturing is in progress, this soluble support material is quickly dissolved with specialized mechanical agitation equipment utilizing a precisely heated sodium hydroxide solution.. GYTE-Makine Mühendisliği Bölümü

  14. 4.2. CAD OutputDevices RapidPrototyping FDM: FusedDepositionModeling GYTE-Makine Mühendisliği Bölümü

  15. 4.2. CAD OutputDevices RapidPrototyping FDM: FusedDepositionModeling GYTE-Makine Mühendisliği Bölümü

  16. 4.2. CAD OutputDevices RapidPrototyping FDM: FusedDepositionModeling FDM ProductExamples: GYTE-Makine Mühendisliği Bölümü

  17. 4.2. CAD OutputDevices RapidPrototyping SLS: SelectiveLaserSintering Laser Sintering is also a technique by which parts are built layer by layer. The basic material consists of powder with particle sizes in the order of magnitude of 50 µm. Successive powder layers are spread on top of each other. After deposition, a computer controlled CO2 laser beam scans the surface and selectively binds together the powder particles of the corresponding cross section of the product. During laser exposure, the powder temperature rises above the glass transition point after which adjacent particles flow together. This process is called sintering. After production of the part is completed powders that function as support material are cleaaned by a brush. The material those are used in this technology are Polyamide, Ploystrene and several metal alloys. GYTE-Makine Mühendisliği Bölümü

  18. 4.2. CAD OutputDevices RapidPrototyping SLS: SelectiveLaserSintering SLS WorkingPrinciple: In sintering powder material is left under the melting temperature of the material so that powders stick to each other. 4 phases of sintering can be seen in the above figure. GYTE-Makine Mühendisliği Bölümü

  19. 4.2. CAD OutputDevices RapidPrototyping SLS: SelectiveLaserSintering • Best application areas of SLS technology • Mechanical and thermal test parts • Plastic parts • Large complex functional parts • Casting parts • Functional models • SLS Advantages • Products are resistant to shape and functional tests • Parts can be assembled with mechanic or chemical methods • No need to use support material • Parts are cleaner than other methods • Heat treatment or painting can be applied on the parts The materials used plastic, metal or ceramic powders can be used, as well as their mixtures consisting of composite powders are also available. Glass fiber reinforced plastic powders or plastic-coated metal powders are examples to this. Inthecase of metal usage themethod is called as Direct Metal LaserSintering (DMLS). GYTE-Makine Mühendisliği Bölümü

  20. 4.2. CAD OutputDevices RapidPrototyping SLS: SelectiveLaserSintering GYTE-Makine Mühendisliği Bölümü

  21. 4.2. CAD OutputDevices RapidPrototyping SLS: SelectiveLaserSintering GYTE-Makine Mühendisliği Bölümü

  22. 4.2. CAD OutputDevices RapidPrototyping SLS: SelectiveLaserSintering SLS ProductExamples: GYTE-Makine Mühendisliği Bölümü

  23. 4.2. CAD OutputDevices RapidPrototyping SLS: SelectiveLaserSintering SLS ProductExamples: GYTE-Makine Mühendisliği Bölümü

  24. 4.2. CAD OutputDevices RapidPrototyping SLS: SelectiveLaserSintering SLS Advantages • SLS polyamide (nylon) material enables full functional prototype production. • Glass-filled nylon is resistant to high temperature and chemical environments in the prototype production. • Rubber like parts can be manufactured directly from polymer. This is for seals and sealing elements that are exposed to high temperature. • For durable metal parts and molded parts P20 steel which is similar to St 200 can be used. SLS Disadvantages • The surface finish of SLS parts are not good as SLA parts but additional surface finish can be applied. • High shrinkage ratios can result torsion, bending or dimensional inaccuracy. • SLS feature details are not precise as in SLA. GYTE-Makine Mühendisliği Bölümü

  25. 4.2. CAD OutputDevices RapidPrototyping SLA: Stereolithography • Stereolithography is an additive manufacturing process using a vat of liquid UV-curablephotopolymer "resin" and a UVlaser to build parts a layer at a time. On each layer, the laser beam traces a part cross-section pattern on the surface of the liquid resin. Exposure to the UVlaser light cures, or, solidifies the pattern traced on the resin and adheres it to the layer below. • After a pattern has been traced, the SLA's elevator platform descends by a single layer thickness, typically 0.05 mm to 0.15 mm (0.002" to 0.006"). Then, a resin-filled blade sweeps across the part cross section, re-coating it with fresh material. On this new liquid surface, the subsequent layer pattern is traced, adhering to the previous layer. A complete 3-D part is formed by this process. After building, parts are cleaned of excess resin by immersion in a chemical bath and then cured in a UV oven. • Stereolithography requires the use of support structures to attach the part to the elevator platform and to prevent certain geometry from not only deflecting due to gravity, but to also accurately hold the 2-D cross sections in place such that they resist lateral pressure from the re-coater blade. Supports are generated automatically during the preparation of 3-D CAD models for use on the stereolithography machine, although they may be manipulated manually. Supports must be removed from the finished product manually; this is not true for all rapid prototyping technologies. GYTE-Makine Mühendisliği Bölümü

  26. 4.2. CAD OutputDevices RapidPrototyping SLA: Stereolithography GYTE-Makine Mühendisliği Bölümü

  27. 4.2. CAD OutputDevices RapidPrototyping SLA: Stereolithography GYTE-Makine Mühendisliği Bölümü

  28. 4.2. CAD OutputDevices RapidPrototyping SLA: Stereolithography GYTE-Makine Mühendisliği Bölümü

  29. 4.2. CAD OutputDevices RapidPrototyping SLA: Stereolithography SLA Part Examples: GYTE-Makine Mühendisliği Bölümü

  30. 4.2. CAD OutputDevices RapidPrototyping SLA: Stereolithography SLA Part Examples: GYTE-Makine Mühendisliği Bölümü

  31. 4.2. CAD OutputDevices RapidPrototyping LOM:LaminatedObjectManufacturing Laminated object manufacturing (LOM) is a rapid prototyping system developed by Helisys Inc. In it, layers of adhesive-coated paper, plastic, or metal laminates are successively glued together and cut to shape with a knife or laser cutter. The process is performed as follows: Sheet is adhered to a substrate with a heated roller. Laser traces desired dimensions of prototype. Laser cross hatches non-part area to facilitate waste removal. Platform with completed layer moves down out of the way. Fresh sheet of material is rolled into position. Platform moves up into position to receive next layer. The process is repeated. GYTE-Makine Mühendisliği Bölümü

  32. 4.2. CAD OutputDevices RapidPrototyping LOM:LaminatedObjectManufacturing Advantages • Low cost due to readily available raw material • Relatively large parts may be made, because no chemical reaction is necessary • Fast as laser only traces the contour and does not trace the whole cross section. • Parts can be used immediately after processing. There is no need for Additional processing. • No need for additional support. • It is easy to use. Disadvantages • The most common used material is still paper. The materials on any other specified is currently underway. • As parts are easily to accommodate to humidity finishing should be applied with a special Epoxy based material (Lompoxy: generated for LOM usage). • Production of complex parts are difficult. • There may be fire problem when the working zone gets too hot. GYTE-Makine Mühendisliği Bölümü

  33. 4.2. CAD OutputDevices RapidPrototyping LOM:LaminatedObjectManufacturing GYTE-Makine Mühendisliği Bölümü

  34. 4.2. CAD OutputDevices RapidPrototyping LOM:LaminatedObjectManufacturing LOM Part Examples: GYTE-Makine Mühendisliği Bölümü

  35. 4.2. CAD OutputDevices RapidPrototyping LOM:LaminatedObjectManufacturing GYTE-Makine Mühendisliği Bölümü

  36. 4.2. CAD OutputDevices RapidPrototyping EBM:ElectronBeamMelting • Electron beam melting (EBM) is a type of additive manufacturing for metal parts. The technology manufactures parts by melting metal powder layer per layer with an electron beam in a high vacuum. • Unlike some metal sintering techniques, the parts are fully dense, void-free, and extremely strong. The vacuum environment in the EBM machine maintains the chemical composition of the material and provides an excellent environment for building parts with reactive materials such as titanium alloys. The electron beam’s high power ensures a high rate of deposition and an even temperature distribution within the part, which gives a fully melted metal with excellent mechanical and physical properties. . GYTE-Makine Mühendisliği Bölümü

  37. 4.2. CAD OutputDevices RapidPrototyping EBM:ElectronBeamMelting • Part surface quality is very good compared to other RP methods. • Can be applicable to metals, materials apart from metals, ceramics and composite materials. • EBM is successful in small and parts with precise regions. • Can drill holes with one or two nanometer precision. • More precise than metal cutting operations. • The part can directly be used after the operation. • No need for extra heat treatment • SLS,LSM,DMLS needs heat treatment. • Due to high energy and scanning method EBM is very fast. • Minimum layer thickness: 0.05 mm • Tolerance: +/-0,4 mm. • Very successful in titanium alloys. • Applied to medical implants, aerospace/automotive parts successfully. • In this method parts are produced within hours. GYTE-Makine Mühendisliği Bölümü

  38. 4.2. CAD OutputDevices RapidPrototyping EBM:ElectronBeamMelting GYTE-Makine Mühendisliği Bölümü

  39. 4.2. CAD OutputDevices RapidPrototyping EBM:ElectronBeamMelting EBM applicationwithTi6AI4Vmaterial GYTE-Makine Mühendisliği Bölümü

  40. 4.2. CAD OutputDevices RapidPrototyping EBM:ElectronBeamMelting • Advantages • Obtaining high energy with narrow beam. • The quality of the vacuum melting enables high material properties. • Vacuum environment avoids oxide and nitride based impurities. • Enables welding of unlike metals that are hard to process. • Comparison with SLS: • Due to efficient beam formation power consumption is low • Maintenance and installation costs are lower • It has high power and speed • Bending of the beam is obtained without moving the part which results high speed and low maintenance. • Disadvantages • Vacuum requirement means additional cost. • Emits gamma rays during operation (Vacuum tanks should be designed to protect rays) • Materials should have electric conductive property. GYTE-Makine Mühendisliği Bölümü

  41. 4.2. CAD OutputDevices RapidPrototyping EBM:ElectronBeamMelting EBM PartExamples: GYTE-Makine Mühendisliği Bölümü

  42. 4.2. CAD OutputDevices RapidPrototyping 3D Printing • Developed in MIT (Massachusetts Institute of Technology). • 3D parts is produced layer by layer. • 3D printers are generally fast and have low costs. • One version of 3D printing includes inkjet printing system. • Fine dust material (plaster, resin) is sprayed from the printer and adhesive is then used for bonding. • This technology enables the production of fully colorful prototypes. GYTE-Makine Mühendisliği Bölümü

  43. 4.2. CAD OutputDevices RapidPrototyping 3-D Printing GYTE-Makine Mühendisliği Bölümü

  44. 4.2. CAD OutputDevices RapidPrototyping 3-D Printing GYTE-Makine Mühendisliği Bölümü

  45. 4.2. CAD OutputDevices RapidPrototyping 3-D Printing 3-D PrintingPartExamples: GYTE-Makine Mühendisliği Bölümü

  46. 4.2. CAD OutputDevices RapidPrototyping RapidPrototyping RP Technology comrarison (lowergrade is better) GYTE-Makine Mühendisliği Bölümü