Professor : Dr. Yu-Sen Yang Speaker : Jia-Hau Lin Date : 2011.05.20

Effects of target current on the mechanical properties of Cr-C coatings by using the Unbalanced Magnetron Sputtering. Professor : Dr. Yu-Sen Yang Speaker : Jia-Hau Lin Date : 2011.05.20. Outline. Introduction Experiment Results and discuss Conclusion. Introduction.

thy
Download Presentation

Professor : Dr. Yu-Sen Yang Speaker : Jia-Hau Lin Date : 2011.05.20

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Effects of target current on the mechanical properties of Cr-C coatings by using the Unbalanced Magnetron Sputtering Professor: Dr. Yu-Sen Yang Speaker:Jia-Hau Lin Date : 2011.05.20

  2. Outline Introduction Experiment Results and discuss Conclusion

  3. Introduction 1.The chromium carbide (Cr-C) films have excellent properties including chemical stability, oxidation resistance, low coefficient of friction and wear resistance. 2. The excellent anti-wear performance of Cr-C films can be attributed to the large content of carbide. 3. Cr-C coatings have been known to protected tools which may be damaged by high thermal load (high cutting speed).

  4. Experiment (equipment)

  5. Experiment (parameter) 資料來源:黃文毅,2010,利用非平衡磁控濺鍍Cr-C薄膜機械性質之研究,國立高雄第一科技大學,碩士論文

  6. Experiment (Properties test) 1.Component Analysis: EDS 2.Morphology: FE-SEM 3.Microstructure: Raman Analysis 4.Friction coefficient: Ball-on-disc

  7. Experiment (Properties test) 5.Wear rate estimation: Calculated after measuring wear track by Alpha-step (1)Alpha-Step量測磨痕斷面面積 (2)計算磨耗體積及磨耗率 V:體積,R:質心半徑,A:不規則形狀面積

  8. Results and discuss (ComponentAnalysis)

  9. Results anddiscuss(Friction coefficient test)

  10. Results anddiscuss (Wear rate) 單位:mm3‧N-1‧m-1

  11. Results and discuss (friction coefficient)

  12. Results and discuss (Wear rate)

  13. Results and discuss 1A 6A

  14. Results and discuss(Raman) D band :1350 cm-1 G band:1580 cm-1

  15. Conclusions The experimental results show the carbon content in Cr-C films increase with decreasing target current when target current decrease from 6A to 1A,the carbon content increase from31.1 at.% to at 94.2 at.% . The friction coefficient of films decrease from 0.66 to 0.22 and the wear rate is reduced from 423‧10-6 (mm3‧N-1‧m-1) to 6‧10-6 (mm3‧N-1‧m-1) when the current reduced from 6A to 1A. The lowest wear rate is 6‧10-6 (mm3‧N-1‧m-1) at traget current 1A The lowest friction coefficient is 0.22at traget current 2A The excellent anti-wear performance of Cr-C films can be attributed to the large content of carbide.

  16. The reasons for a low coefficient of friction is the formation of solid solution carbon in the diamond-like carbon film in the crystal structure, which could effectively reduce wear and promote the wear resistance characteristics.

  17. The End