K. Ioakeimidi, T. Maruyama, J.E. Clendenin, A. Brachmann Stanford Linear Accelerator Center

Polarization comparison of InAlGaAs/GaAs superlattice photocathodes having low conduction band offset. K. Ioakeimidi, T. Maruyama, J.E. Clendenin, A. Brachmann Stanford Linear Accelerator Center Yu.A.Mamaev, L.G.Gerchikov, Yu.P.Yashin, D. Vasilyev St. Petersburg State Polytechnic University

tania
Download Presentation

K. Ioakeimidi, T. Maruyama, J.E. Clendenin, A. Brachmann Stanford Linear Accelerator Center

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Polarization comparison ofInAlGaAs/GaAssuperlattice photocathodes having low conduction band offset • K. Ioakeimidi, T. Maruyama, J.E. Clendenin, A. Brachmann • Stanford Linear Accelerator Center • Yu.A.Mamaev, L.G.Gerchikov, Yu.P.Yashin, D. Vasilyev • St. Petersburg State Polytechnic University • V.M.Ustinov and A.E.Zhukov • Ioffe Physico-Technical Institute • R. Prepost • University of Wisconsin

  2. 85-90%

  3. Main depolarization mechanisms 100nm • Interband absorption smearing d due to bandedge fluctuations • Hole scattering between HH and LH states causes a LH broadening g • Optical phonon scattering • Non polarized electrons generated in the BBR • Scattering of electrons in the BBR electron 6nm GaAs D E c BBR Conduction Band AlGaAs Vacuum Buffer HH1 D E v Valence Band LH1 HH- LH separation determined by well/barrier thickness and strain DEC/DEV determined by SL structure

  4. Motivation for a flat Conduction Band structure • Observed emission spectrum • Emitted electron polarization a: optical absorption R: reflection coefficient t1: electron lifetime in BBR tem: time of electron emission in vacuum  P0: initial electron polarization upon excitation with circularly polarized light S0: surface recombination velocity tS : spin relaxation time in SL tS1 : spin relaxation time in BBR A. Subashiev et. al. SLAC-PUB 10901

  5. 100nm electron 6nm GaAs D E Vacuum c AlGaAs Conduction Band BBR Buffer HH1 D E v Valence Band LH1 Design of a flat conduction band structure Strained Barrier AlyInxGa1-x-yAs/GaAs SL on GaAs substrate y: determines the bandgap x: lowers bandgap, controls DEC and induces strain DEC(x,y)=QC1*DEg1(x)+QC2,def*(DEg2(y)+dEC,def) Yu. A. Mamaev et al., PST2003

  6. Unstrained wells and compressively strained barriers GaAs/AlyInxGa1-x-yAs SL GaAs E c2 e1 E G c1 6 Al In Ga As 0.21 0.20 0.62 E hh1 G v1 8 E lh1 vh2 E vl2 • dQW(Å) E hh2E lh1 E hh1E e1 • 10 -0.2054E+00 -0.1160E+00 -0.5120E-01 1.429 • 15 -0.1752E+00 -0.1041E+00 -0.4413E-01 1.429 • 20 -0.1542E+00 -0.9352E-01 -0.3794E-01 1.428 • 25 -0.1389E+00 -0.8409E-01 -0.3267E-01 1.428 • 40 -0.9484E-01 -0.6199E-01 -0.2145E-01 1.427 Yu. A. Mamaev et al., Mainz 2004

  7. Photocathodes QW: 1.5nm QB: 4nm BBR: 6nm SL doping: 4e17cm-3 GaAsP/GaAs SL: 89meV LH-HH splitting DEC=36meV, DEV=19meV

  8. #5506: In.17Al.18Ga.65As/GaAs SL Green curve – without BBR absorption; Black curve – with BBR

  9. #5501: In.20Al.21Ga.59As/GaAs SL Green curve – without BBR absorption; Orange curve – with BBR

  10. #5503: In.23Al.25Ga.52As/GaAs SL Green curve – In0.23Al0.25Ga0.54As – 1.5 nm GaAs without BBR absorption Blue curve – , In0.23Al0.23Ga0.54As – 1.5 nm GaAswithout BBR absorption; Black curve – In0.23Al0.23Ga0.54As – 1.5 nm GaAs with BBR

  11. #5777: In.20Al.23Ga.59As/GaAs SL 92%

  12. Simulations vs data analysis • Data indicates a blue shift for the polarization peak for samples 5501, 5503, 5506 • In theory longer wavelengths give higher polarization because they obey better the selection rules • In practice longer wavelengths photogenerate electrons primarily in the BBR where there is no polarization selectivity and also • the electrons photogenerated in the SL structure in this case thermalize more in the BBR and they have lower tunneling probabilities due to tighter confinement and due to the CB peak at the interface between the SL and the BBR.

  13. #6329: In.20Al.22Ga.58As/GaAs SL St. Petersburg 78% CTS 76 ~ 77%

  14. #6410: In.28Al.35Ga.37As/GaAs SL St. Petersburg 74% CTS 77%

  15. (004) X-ray 5-777 is better Superlattice thickness: 5-777 5.01 nm 5501 5.10 nm Indium fraction (assume 100% strain): 5-777 19.6% 5501 20.7%

  16. (004) simulation Assume 100% strain

  17. Summary of Polarization Results

  18. How can we explain 90%? • Polarization calibration seems OK within 2-3%. • 5-777 had an As-cap, allowing a low temp heat-cleaning. • When 5-777 was heated to >540 C, polarization dropped to 84%, which is consistent with SVT-5501. • Surface effect supported by the temperature of the heat cleaning dependence of the results • X ray shows decreased barrier size that would imply higher strain • Strained barrier structures do not preserve strain in the BBR; we think that 5777 might have reduced BBR thickness.

  19. Conclusions • The flat CB structures show promising polarization results with a record polarization of 92%. • Further analysis needs to be done in order to understand depolarization effects primarily in the BBR. • The flat CB photocathodes show sensitivity to heat cleaning temperature. The heat cleaning effect needs to be explored further with SIMS analysis.

  20. More SVT results SVT-5506 SVT-5503

  21. SVT-5501 (5-777 duplicate) Peak polarization ~84%

  22. Dear Takashi, We have analyzed your recent data on SL-5501-5506 and agree with your conclusion that the polarization losses could be due to the surface effect. To confirm this assumption we compare your experimental data (points) with our calculations (curves - see figures below). First we calculate the initial polarization of photoelectrons in the working layer using your data of layer composition and thickness. Then we reduce the resulting polarization of emitted electrons by 5% due to the polarization losses in the surface region (. “Energy resolved spin-polarized electron photoemission from strained GaAs/GaAsP heterostructure”, Yu.A.Mamaev, A.V.Subashiev, Yu.P.Yashin, H.-J.Drouhin and G.Lampel, Solid State Comm., Vol. 114, No 7, 2000, pp 401-405.). We have reasonable agreement between the theory and experiment for the overall behavior of polarization spectra for SL 5501 and 5506. For SL 5503 the agreement can be achieved if we assume that the actual Al concentration in barrier layer is 2% lower, i.e. SL 5503 4 nm In0.23Al0.23Ga0.56As – 1.5 nm GaAs. However there is a systematical discrepancy between the theory and experiment in the region of polarization maximum, namely experimental peak is blue shifted and smaller in amplitude. In our calculations the position of the polarization maximum is close to the photoabsorption edge. The QY spectrum behavior near the edge evidences that the position of photoabsorption edge is calculated correctly. Thus the observed blue shift of polarization maximum and large polarization losses might be caused by an additional physical reason.

  23. We assume that this effect can arise from the photoabsorption in the surface (BBR) layer (see our last joint paperA. V. Subashiev, L. G. Gerchikov, Yu. A. Mamaev, Yu. P. Yashin, J. S. Roberts, D.-A. Luh, T. Maruyama, and J. E. Clendenin “Strain-Compensated AlInGaAs-GaAsP Superlattices for Highly-Polarized Electron Emission”, Appl. Phys. Lett. 86 (2005) 171911). In figures below we show the polarization spectra accounting for the BBR contribution to electron emission. Figures demonstrate that this contribution cuts the red side of the polarization maximum resulting in its sizable blue shift and decreasing of amplitude. The similar effect we also observe in SL 6-329 and 6-410. However it seems that in our best sample, SL 5-777, there is no visible BBR contribution. In the last figure we show the polarization spectrum of SL 5-777 together with our calculations. We use the latest Ioffe PTI data on its composition. According to this data SL 5-777 is 3.6 nm In0.20Al0.23Ga0.57As – 1.5 nm GaAs. The barrier thickness we reduce by 0.4nm according to X-ray results, though this change does not almost affect the polarization spectrum. Figure show that our calculations without BBR contribution (initial polarization – 5% surface losses) reproduce well the experimental spectrum. Unfortunately we do not understand at the moment why some samples are good and some samples with close or even the same design are bad.

  24. 100nm electron 6nm GaAs Vacuum D E c AlGaAs HH1 D E Conduction Band BBR Buffer v Valence Band LH1

  25. InAlGaAs-GaAs superlattice • St. Petersburg group observed 90% polarization from InAlGaAs-GaAs superlattice (5-777). • SVT grew three wafers • 5506: 4 nm In0.17Al0.18Ga0.59As – 1.5 nm GaAs 18 periods • 5501: 4 nm In0.20Al0.21Ga0.59As – 1.5 nm GaAs 18 periods (duplicate of 5-777) • 5503: 4 nm In0.23Al0.25Ga0.59As – 1.5 nm GaAs 18 periods • Peak polarization of SVT-5501 was 84%. • Three samples from St. Petersburg • 5-777 Could not activate to high enough QE. No measurements. • 6-329 4 nm In0.2Al0.22Ga0.58As – 1.5 nm GaAs 18.5 periods • 6-410 3.07 nm In0.28Al0.354Ga0.366As – 0.56 nm GaAs 15 periods • X-ray diffraction of Ioffe 5-777 and SVT-5501