An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Metal Casting II Manufacturing Processes

  2. Outline • Sand Casting • Shell Mold Casting • Composite Molds • Expendable Pattern Casting • Plaster Mold Casting • Ceramic Mold Casting • Investment Casting • Pressure Casting • Vacuum Casting • Die Casting • Centrifugal Casting • Squeeze Casting and Semisolid Metal Forming • Casting Single Crystals • Rapid Solidification • Melting • Design Considerations

  3. Examples of Cast Parts

  4. Examples of Cast Parts

  5. Typical Casting Metals Aluminum Aluminum-silicon alloy Aluminum-copper Brass Gray cast iron Copper Lead Steel

  6. Casting Processes

  7. Sand Casting Uses a mold made of compressed sand; after the metal solidifies, the sand is broken away

  8. Sand Casting Pattern Full sized model of the part Core Full sized model of the interior surfaces of the part Sand Silica (SiO2) 90% sand 3% water 7% clay

  9. Sand Casting

  10. Sand Casting

  11. Example of a Sand Casting Mold

  12. Sand Casting Advantages: Almost no limit on size, shape, weight or complexity; low cost; almost any metal Limitations: Relatively poor tolerances and surface finish; machining often required; low production rate Common metals: Cast irons, steel, stainless steel, casting alloys of aluminum and copper, magnesium and nickel

  13. Sand Casting Size limits: 1 oz – 6000 lb Thickness limits: As thin as 3/32 in, no maximum Tolerances: 1/32 in for the first 6 in, .003 in for each additional inch; additional increment across the parting line Draft allowance: 1 - 3° Surface finish: 100 -1000 µin

  14. Shell Casting Casting process in which the mold is a thin shell (typically 3/8 inch) made of sand held together by a thermosetting binder

  15. Shell Casting

  16. Shell Casting Advantages: Higher production rate than sand casting; high dimensional accuracy and smooth finish Limitations: Requires expensive metal patterns; resin adds to cost; part size is limited Common metals: Cast irons, casting alloys of aluminum and copper

  17. Shell Casting Size limits: 1 oz minimum; usually less than 25 lb; mold area usually less than 500 in2 Thickness limits: 1/16 – ¼ in depending on material Tolerances: .005 in/in Draft allowance: ¼ - ½° Surface finish: 50 – 150 µin

  18. Composite Molds Made from 2 or more different materials Good for complex shapes such as turbine blades

  19. Expendable Pattern Casting Polystyrene pattern vaporizes on contact with molten metal

  20. Foam Pattern of an Engine Block

  21. Plaster Mold Casting Uses a mold made of plaster (gypsum) with talc and silica, which is broken away after the metal solidifies The mold has a relatively low thermal conductivity; a somewhat uniform grain structure can be produced

  22. Plaster Mold Casting Advantages: High dimensional accuracy and smooth finish; can make net- or near-net-shaped parts Limitations: Lower temperature nonferrous metals only; long molding time; mold material is not reusable; maximum size limited Common metals: Primarily aluminum and copper

  23. Plaster Mold Casting Size limits: 1 oz – 15 lb Thickness limits: As thin as .025 in Tolerances: .005 in on the first 2 in; .002 in per additional inch Draft allowance: ½ - 1° Surface finish: 50-125 µin

  24. Ceramic Mold Casting Uses a mold made of refractory ceramic materials which can be used for high-temperature applications

  25. Ceramic Mold Casting

  26. Ceramic Mold Casting Advantages: Intricate detail, close tolerances, smooth finish Limitations: Mold material is expensive and not reusable Common metals: Ferrous and high-temperature nonferrous metals are most common; can be used with alloys of aluminum, copper, magnesium, titanium and zinc

  27. Ceramic Mold Casting Size limits: Several ounces to several tons Thickness limits: As thin as .05 in, no maximum Tolerances: .005 in on the first inch; .003 in per additional inch Draft allowance: 1° Surface finish: 75-150 µin

  28. Investment Casting Uses a wax pattern which is coated with refractory materials to form a mold; the wax is then melted out and the mold cavity is filled with metal Can be used for high precision complex shapes from high melting point metals that are not readily machinable

  29. Investment Casting

  30. Example of a Wax Injection Mold

  31. Example of a Wax Pattern

  32. Example of a Coated Pattern

  33. Example of Finished Castings

  34. Investment Casting Advantages: Excellent surface finish; high dimensional accuracy; nearly unlimited intricacy; almost any metal; no flash or parting line Limitations: Expensive patterns and molds; high labor costs; limited size Common metals: Mainly aluminum, copper and steel; also used with stainless steel, nickel, magnesium and precious metals

  35. Investment Casting Size limits: As small as 1/10 oz; usually less than 10 lb Thickness limits: As thin as .025 in, less than 3 in Tolerances: .005 in on the first inch; .002 in per additional inch Draft allowance: none required Surface finish: 50-125 µin

  36. Pressure Casting Pressure casting forces the metal up into the mold chamber by applying a small amount of pressure

  37. Vacuum Casting

  38. Permanent Mold Casting (Pressure/Vacuum) Advantages: Good surface finish and dimensional accuracy; metal mold causes rapid cooling and fine grain structure; molds can be used up to 25 000 times Limitations: High initial mold cost; shape, size and complexity are limited; mold life is very limited with metals with high melting points Common metals: Alloys of aluminum, magnesium and copper most common; iron and steel can be used in graphite molds; alloys of lead, tin and zinc also used

  39. Permanent Mold Casting (Pressure/Vacuum) Size limits: Several ounces to about 150 lb Thickness limits: Minimum depends on material but generally thicker than 1/8 in; maximum about 2 in Tolerances: .015 in for the first inch and .002 in for each additional inch; .01 in added across the parting line Draft allowance: 2 - 3° Surface finish: 100 - 250 µin

  40. Die Casting Another form of permanent mold casting; molten metal is forced into the mold cavity at pressures ranging from .7 MPa - 700 MPa

  41. Die Casting

  42. Die Casting

  43. Example of a Die Casting Mold

  44. Centrifugal Casting Uses a rotating mold to form hollow cylindrical parts such as pipes, gun barrels and lamp posts

  45. Vertical Centrifugal Casting

  46. Centrifugal Casting Advantages: Can produce a wide range of cylindrical parts; good dimensional accuracy and cleanliness Limitations: Limited shape; spinning equipment may be expensive Common metals: Iron, steel, stainless steel, alloys of aluminum, copper and nickel

  47. Centrifugal Casting Size limits: Up to 10 ft in diameter and 50 ft in length Thickness limits: Wall thickness .1 – 5 in Tolerances: Outer diameter within .1 in; inner diameter within about .15 in Draft allowance: 1/8 in / ft Surface finish: 40 - 100 µin

  48. Semicentrifugal Casting Uses a rotating mold to form parts with radial symmetry, such as wheels with spokes

  49. Squeeze Casting A combination of casting and forging; a die applies pressure as the metal solidifies

  50. Casting Single Crystals Uses a slow crystal-growth solidification procedure to produce parts made of a single crystal with no grain boundaries A helical constriction only allows one crystal of favorable orientation to grow into and fill the mold chamber