Lecture Notes II Defect Chemistry

Lecture Notes II Defect Chemistry. Ole Toft Sørensen (Risoe National Laboratory) Ceramic Materials Consultant Email:otsdk@yahoo.dk. Electroceramics. Electrical properties determined by defects. Knowledge of defect chemistry necessary to understand Electroceramics!. What is a defect?.

Download Presentation

Lecture Notes II Defect Chemistry

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Lecture Notes IIDefect Chemistry Ole Toft Sørensen (Risoe National Laboratory) Ceramic Materials Consultant Email:otsdk@yahoo.dk

  2. Electroceramics • Electrical properties determined by defects • Knowledge of defect chemistry necessary to • understand Electroceramics!

  3. What is a defect? Fundamental definition:Any deviation from the perfect crystal is a defect! - Macroscopic defects (porosities, cracks) • Atomic defects • Electronic defects

  4. Atomic (point) defects in Oxides! Missing ions: - oxygen ions, oxygen vacancies - cations, cation vacancies Substituted ions Interstitiel ions

  5. Electronic defects in oxides • Atomic (point) defects – type, properties depend on position ! • Electronic defects – type, properties depend on energy levels • available for the electrons • electrons • positive holes

  6. Defect notations subscript (Symbol for type)position VO = vacancy on oxygen position VM = vacancy on metal position, VFe Oi = interstitial oxygen ion Mi = interstitial cation YZr = Y-ion on Zr-ion position

  7. Charges of defects Relative chargeCharge relative to the charge normally present in the position of the defect Examples: ZrZr – relative charge = zero, but YZr - relative charge = -1 FeO: Fe2+ vacancy – rel. ch. = ? -2 of course! ZrY ? Rel. ch.+1

  8. Charges of oxygen vacancies Formation of oxygen vacancies: Oxygen atoms are removed from the crystal Oxygen ions – how many electron in outer orbital ? 8 Oxygen atoms – how many electrons in outer orbital ? 6 2 Oxygen vacancy – how many electrons left ? Rel. Charge ? Zero! But these electrons can easily migrate to neighbouring ions forming vacancies with one or zero electrons present. Thus VO with rel. charges of zero, +1 and +2 can be formed !

  9. Relative charges of interstitial ions -2 O2- ions,Oi ? Cl-1 – ions, Cli, rel. charge = -1 Na+1 – ions, Nai , ? +1 Zr4+ - ions, Zri, rel. charge = +4

  10. Nomenclature: relative charges • Relative charges are indicated by a superscript: • neutral - x • positive charges – black dots • negative charges - apostrophes Examples: Neutral: VOx Positive charges: VO•, VO•• Negative charges: VFe″

  11. Practise: Nomenclature

  12. Answers to practise

  13. Formation of defects Three typical areactions: - ”high” temperatures, INTRINSIC DEFECTS - reaction with surrounding atmosphere - substitution

  14. Intrinsic defects Pair of defects: • Frenkel defect: • cation vacancy and interstitial cation • Anti-Frenkel defect: • oxygen vacancy and interstitial oxygen ion • Schottky defect: • oxygen vacancy and cation vacancy MO: OOx + MMx = VO•• + VM″ M2O3: 3OOx + 2MMx = 3VO•• + 2VM″′ Stoichiomtry must be maintained !

  15. Defects formed in an reaction with surronding atmosphere. Reduction MO2 = MO2-x+ x/2 O2 OOx + 2MMx = VO•• + 2MM′ + 1/2O2 Oxides with cations easily reduced!

  16. Defects formed in a reaction with a surrounding atmosphere - 2 Oxidation MO + y/2O2 = M1-yO Note – clusters ! Cations easily oxidized!

  17. Formation of interstitial oxygen ions- Oi High oxygen pressures ! 1/2 O2 + 2MMx = Oi″ + 2MM• Oxides where cations are easily oxidized – FeO

  18. Defects formed by substitution! Substitution of cations ! Lower valency: Higher valency: ZrO2 doped with CaO: Y2O3 doped with ZrO2: CaO(ZrO2) = CaZr″ + VO•• + OOx 2ZrO2(Y2O3) = 2ZrY• + Oi″ + 3OO Oxygen vacancies formed to maintain electrical neutrality ! Same valency?

  19. PracticeFormation of Defects

  20. AnswersPractice – Formation of Defects

  21. Dependence on oxygen pressure 1 Can defects in a solid be considered as ions in a solution? • Yes if these conditions are fulfilled: • random distribution of defects • no interactions • high mobility Law of mass action can be used.

  22. Rules which must be obeyed • ratio between cation and anion positions – Constant! • the total number of positions can be changed, • but not the ratio! • neutrality must be maintained

  23. Formation of oxygen vacancies

  24. [VO]  log pO2 1 2

  25. Brouwer plots - VO

  26. Practise:Brouwer plots oxygen vacancies

  27. Answers to practice:Brouwer plots oxygen vacancies

  28. [VM]  log pO2 1 2 3 4 5

  29. Brouwer plots - VM

  30. Practice:Formation of cation vacancies

  31. Answers to practice:Formation of cation vacancies

  32. Brouwer plot for Oi 1 2 3

  33. Brouwer plot:many defects • Construction: • - Log Conc. defect vs log(pO2)- 3 p(O2) regions; • one type of defect dominates in each region • - sharp transition between regions, approximation

  34. Calculation of defect concentrations • Deviation from the stoichiometric composition. • Fraction of defects • Number of defects per cm3

  35. Deviation from stoichiometric composition

  36. Site Fractions MO2-x Fe1-yO MO2+x

  37. Number of defects per cm3

  38. PracticeCalculation of defect concentrations

  39. AnswersCalculaion of defectconcentrations