复合水凝胶材料的制备. 赵 君. Content . 1. 近期实验结果与讨论 2. 后续实验准备与安排. 1. 近期实验结果与讨论. 1) Fmoc -FF 与聚丙烯酰胺复合水凝胶 实验方法： 1. 将 Fmoc -FF 溶解于 NaOH 溶液中，制备 3mg/ml 的溶液，调节 pH 到 11 ； 2. 配置不同浓度的聚丙烯酰胺溶液，并加入 NaOH ，调节 pH 到 11.5 左右； 3. 将溶解后的 Fmoc -FF 溶液与不同浓度的聚丙烯酰胺溶液等体积混合均匀，再滴入适量的 HCl 溶液使之中和 NaOH 。 结果：

salome
Download Presentation

复合水凝胶材料的制备

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 复合水凝胶材料的制备 赵君

  2. Content • 1. 近期实验结果与讨论 • 2. 后续实验准备与安排

  3. 1. 近期实验结果与讨论 1)Fmoc-FF与聚丙烯酰胺复合水凝胶 • 实验方法： • 1.将Fmoc-FF溶解于NaOH溶液中，制备3mg/ml的溶液，调节pH到11； • 2.配置不同浓度的聚丙烯酰胺溶液，并加入NaOH，调节pH到11.5左右； • 3.将溶解后的Fmoc-FF溶液与不同浓度的聚丙烯酰胺溶液等体积混合均匀，再滴入适量的HCl溶液使之中和NaOH。 • 结果： • 1.随着聚丙烯酰胺pH升高，混合体系能够形凝胶，但是稳定性很差。 • 2.凝胶的顶部总是出现一些絮状物质，而且随着聚丙烯酰胺浓度的升高成胶难度会增大。 • 3.胶体易碎，成型能力不强。

  4. 1. 近期实验结果与讨论 2)Fmoc-FF与海藻酸钠复合水凝胶 • 实验方法： • 1. 加热溶解海藻酸钠，制备不同浓度的海藻酸钠溶液，恢复至室温； • 2. 用3mg/ml的Fmoc-FF溶液与海藻酸钠溶液等体积混合均匀，各分成两份，分别先滴加氯化钙溶液和氯化氢溶液成胶； • 3. 取0.15wt%和0.5wt%海藻酸钠混合液，1）先加入HCl中和NaOH，取不同时间的混合液滴入1wt%的氯化钙溶液中成球，2）将混合液滴入氯化钙和氯化氢混合溶液中成球。 • 结果： • 1. 成胶效果都不是很好，胶体不均匀，且有絮状物质； • 2. 加入氯化氢后的混合溶液中，Fmoc-FF成纤维能力很强，无法取出完整液滴； • 3. 通过滴至氯化钙和氯化氢混合溶液中的方法可以成球。

  5. 0.15wt%Fmoc-FF + 0.15wt% SA 球表面 自然晾干

  6. 0.15wt%Fmoc-FF + 0.5wt% SA 球表面 自然晾干

  7. 2. 后续实验准备与安排 • 1. 用聚丙烯酰胺和Fmoc-FF溶液尝试多层结构制备薄膜 • 2. 通过改变条件（滴入方式、浓度等）使海藻酸钠混合溶液制备的微球结构更均一