1 / 9

NANOMATERIALE SI NANOTEHNOLOGII: Realizari si perspective -ICCRR

UNIVERSITATEA BABES BOLYAI CLUJ-NAPOCA INSTITUTUL DE CERCETARI IN CHIMIE « RALUCA RIPAN ». NANOMATERIALE SI NANOTEHNOLOGII: Realizari si perspective -ICCRR. Profilul ICCRR: Cercetări şi produse de sinteză organică şi anorganică fină

palti
Download Presentation

NANOMATERIALE SI NANOTEHNOLOGII: Realizari si perspective -ICCRR

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. UNIVERSITATEA BABES BOLYAI CLUJ-NAPOCA INSTITUTUL DE CERCETARI IN CHIMIE « RALUCA RIPAN » NANOMATERIALE SI NANOTEHNOLOGII: Realizari si perspective -ICCRR • Profilul ICCRR: Cercetări şi produse de sinteză organică şi anorganică fină • Suport financiar: Autofinantare ( proiecte; productie;servicii) • Structura ICCRR: • Laboratoare de Cercetare: • Analize Fizico-Chimice • Biocompozite Polimerice • Chimia Starii Solide • Produsi Naturali • Centrul de Productie Feromoni Workshop “Nanotehnologiile in Transilvania”, Cluj-Napoca mai 2011

  2. 1) CHIMIA STARII SOLIDE – PRODUSE, TEHNOLOGII, SERVICII • ObiectivStudii privind prepararea, caracterizarea si utilizarea unor materiale micro- si nanostructuratecuproprietati controlate pentru aplicatii diverse: electrotehnica, depoluare, optoelectronica etc. Tinta Noi tehnologii: Dezvoltarea unornoicai de sinteza pentru materialele cu proprietati speciale. Noi produse: Obtinerea de noi materiale micro si nano-structurate cu proprietati tintite Rezultat: tehnologii, produse/ brevete de inventie si lucrari stiintifice; • Directii de cercetare specifice( implica sau conduc la materiale nanodimensionate) • Nanopulberi si filme subtiri cu proprietati luminescente: Sulfura de zinc si/sau cadmiu. • Nanopulberi si filme subtiri cu porozitate controlata/cu proprietati speciale: Trioxid de wolfram • Pulberi cu grad de dispersie ridicat: Alumina monohidratata. • Micro-materiale photoluminescente (PL) performante pentru dispozitive de iluminat i.e. diode emitatoare de lumina-LED si/sau tuburi cu descarcare in gaze-GDT

  3. 2) Nanopulberi cu proprietati luminescente: Sulfura de zinc dopata cu mangan Preparare: co-precipitare, sistem Zn-Mn(AcO)2; Tehnica: SeqAdd/SimAdd Caracteristici: Pulbere alba, fina formata din particule sferice <10 nm; Structura cub-ZnS ( Deff ~3 nm); PL intens ~600 nm (ZnS:Mn)  nano-efect. Aplicatii: Dispozitive optoelectronice Na2S Zn(AcO)2 –Mn(AcO)2 Agitare 50 C Agitare 50 C Apă-aditiv C21 -MAA C74 - C75-SDS C21 -MAA C74 - C75-SDS Spălare Uscare Microfotografii (TEM) MicrofotografiiMO (UV-365nm) NP ZnS:Mn Parametri microstructurali (XRD) 1) Chalcogenide Letters 7 (2010) 631-640; 2) IEEEProc-CAS_2010_513-516; 4) Journal of Optoelectronics and Advanced Materials, 10 (2008) pp 2342 – 2345; 3)Studia Universitatis Babes Bolyai Chemia LIV (2009) 23-29;

  4. 3)Filme subtiri cu proprietati luminescente: Sulfura de zinc/cadmiu dopata Preparare: Precipitare, sistem Zn2+/Cd2+ -tiouree; Tehnica CBD ; Dopaj original Caracteristici: straturi subtiri <400 nm pe sticla/ ITO-sticla; Particule sferice 100-200nm, in organizare structurala incipienta hex-ZnS (Deff=14 nm); Aplicatii: Dispozitive optoelectronice ZnS(Cu)/ glass/ ZnS(Cu) ZnS(Mn)/ glass/ ZnS(Mn) ZnS(Cu,Mn)/ glass/ ZnS(Cu,Mn)) ZnS /ITO/glass/ ZnS 1) RO 122546/28.08.2009; 2)Revista de Chimie (Bucuresti), 60 (2009) pp.342-346; 3) Journal of Alloys and Compounds 434-435 (2007) pp. 697-700; 4) Studia Universitatis Babes Bolyai, seria Chemia LI (2) (2006) pp.147-151

  5. 4) Filme subtiri cu proprietati optice speciale Trioxidul de wolfram Preparare: Metodasol-gel/sistem W –H2O2; dip-coating Caracteristici: straturi subtiri de ~200 nm pe ITO; incolore,cu irizari albastre; particule nanometrice, in organizare cristalina incipienta (precursor: mcl-WO3, Deff=4.2 nm); Potential aplicativ: ferestre electrocromice; celule fotoelectrochimice W H2O 2 agitare uscare WO3 x nH2O Depunere dip-coating Reflexie speculara-difuza-totala calcinare WO3/Glass/WO3 WO3/ITO/Glass/WO3 Transmisie inainte/dupa ciclare Imagine SEM frontala/ transversala Voltamograme ciclice Difractograme precursor-film 1) Studia Universitatis Babes-Bolyai, Chemia, LIV, 2009, 15-22; 2) Journal of Optoelectronics and Advanced Materials, 10 (2008) 2261 – 2264; 3) Journal of Alloys and Compounds, 483 (2009) pp.445–449.

  6. 5) Pulberi cu porozitate controlata Trioxidul de wolfram Preparare: Metoda sol-gel, sistem W –H2O2; Dopaj MP/MT Caracteristici: pulbere galbena, mezoporoasa, particule poliedrice 50-100nm, structura mcl-WO3; Aplicatii: fotocataliza/degradarea oxidativa a colorantilor organici Wpwd H2O 2 Microfotografii (TEM) Parametrii microscristalini (XRD): Pt/ Pd Cu/ Mn/ Ni/ Ag Agitare Uscare WO3 x nH2O Distributia porilor (BET) Fotodegradarea colorantilor Agitare Calcinare WO3/Dopant 1) Journal of Optoelectronics and Advanced Materials –Symposia, 2010, 2(1), 115-118. 2) Studia Universitatis Babes-Bolyai, Chemia, XLV, 2010, 2 (I), 169-177.

  7. 6) Nanopulberi cu grad de dispersie controlat Alumina monohidratata ( boehmita) NaOH H2O Al Preparare: precipitare, tehnica SimAdd, Caracteristici: Pulbere alba, inalt dispersa, Particule sferice 10-20nm, Structura orthorombica (boehmita); Suprafata specifica: 290-300 m2/g; Porozitate totala: Vp = 0.301 cm3/g) Aplicatii: *Liant, in compozitii poroase /suport catalitic; *Material de umplutura, in compozitii intumescente/ protectie antifoc, pasiva; *Furnizor de Al2O3 in RSS; Na[Al(OH)4] HNO3 Precipitare Sim-Add AlO(OH) 1) RO 122129/ 30.01.2009; 2) C.B.I. a 2008 00781/01.10.2008 ; 3)Journal of Optoelectronics and Advanced Materials, 6 (2004) 219-224; 4)Studia Universitatis Babes Bolyai, seria Physica XLIX (2004) pp.393-397

  8. 7) Utilizarea nanopulberii de alumina monohidratata PIGMENT FOTOLUMINESCENT DE CULOARE GALBEN INCANDESCENT PENTRU TUBURI DE DESCARCARE IN GAZE SI PROCEDEU DE PREPARARE A ACESTUIA C.B.I. a 2008 00781/01.10.2008 SUPORT CATALITIC MONOBLOC SI PROCEDEU DE CONFECTIONARE A ACESTUIA RO 122129/ 30.01.2009 Titular: UBB-ICCRR si RAAL Bistrita ; Autori: E.J.Popovici, A-M.Valean, V.Pop, A.Hristea –Simoc, M. David, I. Petrutiu Titular: UBB-ICCRR; Autori: E.J.Popovici, L.E.Muresan, M.Morar, A-M.Valean, I.Nemeth Produs nou = compozitie bazata pe utilizarea unui nou luminofor de corectie a culorii (YTA). Proces nou = Procedeu original de preparare a luminoforului de baza YAG, pornind de la boemita Produs nou.Schelet metalic, cu structura fagure de constructie speciala, căptuşit cu un material poros de ~ 20 µm Proces nou. Procedeu original de preparare a stratului poros: -alumină si alumina monohidratata /boemită. Multifunctionalitate. Poate fi incarcat cu metale pretioase/oxizi metalici fin dispersati  Catalizator tip fagure pentru aplicatii de mediu. Compozitie chimica: Aluminat de ytriu dopat cu Ce (YAG) + Tantalat de ytriu dopat cu Eu/Tb (YTA) Caracteristici: Pulbere policristalina galben-portocalie, cu particule poliedrice/ rotunjite1-5um; Fotoluminescenta (254nm): galben-portocaliu (verde-YAG+ rosu YTA) Utilizare: A. Confectionarea tuburilor cu descarcare in gaze pentru reclame luminoase; B. Fabricarea wLED IMT Bucuresti S.C.NEONPRODUCT srl, Cluj-N Medalie de aur EUREKA 2010, Salon INNOVA BRUXELLES Medalie de argint EUREKA 2009, Salon INNOVA BRUXELLES

  9. YAG YGAG(25%) YGAG(50%) YGAG(75%) GAG 8) Micro-materiale luminescenteLuminofori pe baza de oxid de ytriu (tip YO; YAG; YGAG; GAG ) Sarurimetalice Y3+ - Gd3+-Al3+- Ce3+ Agentprecipitare (NH2)2CO Agitare 800 C Apă - Uree Spălare Uscare Nano-Precursor Y-Gd-Al-Ce x M(OH)3· yM(NO3)3· zNH3. vH2O Nanopulbere precursor Gd-Ce-Al Calcinare< 13000C cub-YGAG :Ce Y3-x-y GdxCeyAl5O12 Co-precipitare;Tehnica SimAdd YGAG:Ce Spectre si coordonate cromatice Micropulbere GAG:Ce 1) RO 122856/ 2010 ; 2) CBI a 1099/ 12 nov. 2010; 3) CBI a 2008 00782/01.10.2008; 4) Journal of Alloys and Compounds 497 (2010) 201–209; 5)Radiation Measurements 45(2010) 300-303; 6) Journal of Alloys and Compounds, 471 (2009) pp. 421–427; 7) J. Optoelectron. Adv. Mater.- Symposia (2009), 1(6),1000-1003; 8) Journal of Alloys and Compounds, 434-43(2007) pp.809-812;

More Related