1 / 36

Effect of Alloying Elements on the Eutectoid Decomposition

Effect of Alloying Elements on the Eutectoid Decomposition. Plain Carbon Steels contain: 0.5 – 1.0 % Mn and 0.15 – 0.30 % Si Low Alloy steeels may also contain additional elements such as: Co Cr Mo W Ni V Ti – and may have Mn contents up to 5%

Download Presentation

Effect of Alloying Elements on the Eutectoid Decomposition

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Effect of Alloying Elements on the Eutectoid Decomposition Plain Carbon Steels contain: 0.5 – 1.0 % Mn and 0.15 – 0.30 % Si Low Alloy steeels may also contain additional elements such as: Co Cr Mo W Ni V Ti – and may have Mn contents up to 5% When dissolved in austenite, these alloys can affect the …………. reaction by, • Changing the eutectoid temperature – TE Mn and Ni stabilize ……… and thus ……. the TE to below 727 oC. Si, Cr, and Mo stabilize ..... and thus ………… the TE above 727 oC. Note: the effect of alloying elements on the phase stability of ferrite should not be confused with their effect on the stability of graphite or cementite, which may be quite different.

  2. Effect of Alloying Elements on the Eutectoid Decomposition Alloying additions affecting the eutectoid reaction (cont’d) 2. Lowering the eutectoid composition of the austenite to below 0.77 %C strengthens in the order of Ti>Mo>W>Si>Cr>Mn>Ni. 3. Changing the composition of the ferrite and cementite by partitioning in the pearlite transformation. Note that an element in the g-phase upon cooling does not just go into the a-phase but is ……………. between the ferrite and the cementite phases. What does this mean? 4. Changing the growth rate of pearlite Co is the only element that does not retard the growth of pearlite As, Si, Cr, and Mo raise TE where the degree of undercooling is increased so at temperatures above the “knee” in the TTT diagram, the growth rate is increased whereas at temperatures below the “knee”, the growth rate is decreased.

  3. Effect of Alloying Elements on the Eutectoid Decomposition What is TE for 3% Si? What is %C of eutectoid for 3% Si?

  4. It was noted earlier that the interlamellar spacing, , varies as: Effect of Alloying Elements on Pearlite Lamellar Spacing Where DT is the …………………….. . Plots of 1/l versus temperature are thus linear, with a negative slope as shown by the dashed line for a plain carbon eutectoid steel. The addition of 0.4-1.8 wt% Cr displaces the plot to the right, ie., to ………….. and upwards to …………… lamellar spacing. The addition of 1.08-1.8 %Mn displaces the plot to the left, ie., to lower TE and downwards to larger lamellar spacing. What does Mn stand for?

  5. Temperature Dependence of the Pearlite Transformation At temperatures just below the eutectoid, it can be assumed that: • The nuclei are ………….. distributed throughout the austenite • The average rate of nucleation, N, is ………………. . • The nodules remain ………….. in shape • The growth rate, G, is ………………… . • The fraction of austenite transformation to pearlite as a function of time, f(t) is then given by the Johnson-Mehl equation: This equation gives a typical …………… curve for the fraction transformed as a function of time. A considerably more complex equation is required at lower reaction temperatures when the assumption of random nucleation is no longer valid.

  6. Time-Temperature-Transformation Curves(TTT Curves) Transformation-time curves for a given temperature are derived by examining the …………………….. of samples removed from a furnace after pre-set times. The time, which is taken as the …………. , of the reaction is taken as the time to obtain ……….. of the transformation product. The time, which is taken as the …………., of the reaction is taken as the time to obtain ………… of the transformation. These times are plotted for a series of temperatures to give the TTT curve.

  7. Time-Temperature-Transformation Curves(TTT Curves) The TTT curve is divided into areas, which represent single constituent fields or two component regions. To the left of the 1% pearlite “C-curve” the microstructure is austenitic. To the right of the 99% pearlite “C-curve”, the microstructure is pearlitic. Between the curves, the microstructure is a mixture of austenite and pearlite. The amount of the two constituents can be obtained by plotting further C-curves for 10%P, 20%P, 50%P, etc.

  8. Time-Temperature-Transformation Curves(TTT Curves) The TTT curves are only plotted for temperatures above the “knee” of the temperature dependent growth rate curve for pearlite. As the temperature is lowered to this knee, the time to start the reaction, which is the ………………, is drastically lowered and is a maximum at 600 oC. In plain carbon steels, an ………… in nucleation and growth rate with the degree of undercooling can …………. the incubation period to zero so that the decomposition of austenite cannot be suppressed by rapid quenching. At temperatures below the knee of the C-curve, competing microstructures can become more stable than pearlite. Below the knee of the C-curve, …………. forms isothermally, while …………….. forms “athermally” on quenching below 250 oC as indicated by the horizontal lines at the bottom of the TTT plot.

  9. The Bainite Reaction Bainite is formed over a wide range of temperatures from 200-500 oC. • ………… bainite form in the temperature region 300-500 oC • ………… bainite forms in the temperature region 200-300 oC Bainite – like pearlite – is a mixture of ferrite and carbide, but the …… of the carbide depends on the its temperature of formation. • For upper bainite, the carbide is …………. Fe3C with …………. . • For lower bainite, the carbide is …….. (Hagg carbide) Fe2.2C with …………… . In addition, the physical form of the ferrite and carbide phases are quite different in upper and lower bainite, giving very distinct microstructures.

  10. Upper Bainite Upper bainite formed at 460 oC is composed of a very fine structure composed of laths of ferrite with layers of cementite between the laths. In the electron micrographs taken at 15,000x magnification, the dark regions are packets of ferrite laths and the light regions are cementite.

  11. Upper Bainite Lower bainite formed at 250 oC is much courser and the e-carbide particles are precipitated with the ferrite. In the electron micrographs taken at 15,000x magnification, the ferrite plates are a more regular and needle-like in shape while the carbide particles are smaller in size and appear as striations at an angle of 55 degrees to the axis of the plate.

  12. The isothermal decomposition of austenite to bainite follows a typical ……….. , which can be analyzed by the Johnson-Mehl equation. This equation was used to generate the solid line in the transformation plots for bainite reaction at 150-390 oC in a 1.1% C hypereutectoid steel. The experimental data conform closely to the equation at high temperature but deviate at the lower temperatures, which in fact lie below the Ms of the steel, ie., the martensitic transformation temperature, at ~180 oC. On this basis, the bainite reaction can be classified as a ………………………… …………………………………………………………………….. . Kinetics of the Bainite Reaction

  13. The isothermal decomposition of austenite to upper and lower bainite can be separated into ……………………. TTT curves by the addition of alloying elements such as Si, which slow down the formation of carbides. This has been demonstrated in a steel containing 0.43 C, 3.0 Mn, and 2.12 Si. In the plots below, the solid lines refer to 5% transformation, while the dotted lines indicate the experimental scatter of the data. TTT Curves of the Bainite Reaction

  14. Metallurgists have been arguing for more than 50 years about the mechanism of the bainite transformation mechanism. This has arisen because it does not fit precisely under either diffusion controlled nucleation and growth transformations like pearlite or shear controlled transformations like martensite. A solution to this dilemma has been suggested by Ko and Cottrell: • Austenite transforms to ferrite by a martensitic shear transformation • Substitutional solutes remain in the same positions relative to the Fe atoms • In upper bainite, the carbon diffuses in the austenite to form cementite • In lower bainite, the carbon diffuses in the ferrite to form e-carbide Hence the initial phases form by shear and then diffusion of carbon controls the growth of both the carbide phases. Mechanism of the Bainite Reaction

  15. The horizontal lines on TTT diagrams refer to the formation of martensite. Ms is the highest temperature at which martensite forms on cooling • Martensite can form by deformation at temperatures > Ms and < Md M50 and M90 are the temperatures at which these percentages of martensite form. Mf is the lowest temperature at which martensite forms on cooling although the transformation may not be 100% completed at Mf These characteristics are referred to as “……………” as opposed to isothermal. The Martenisitic Transformation Athermal martensitic transformation in 0.40% C low alloy steel Effect of carbon concentration on Ms and Mf .

  16. The crystal structure of a-ferrite is ………. with the carbon atoms ……… distributed among the interstitial sites. As the maximum concentration of C is 0.02 wt%, very few of the available carbon interstitial sites are actually occupied so the structure remains cubic. The Martenisitic Phase in Steels

  17. In a`-matensite, the carbon atoms are restricted to interstitial sites at the centres of the crystal faces and the unit cell’s edges that lie parallel to the c-axis. This selective occupation of interstitial sites causes the c-axis to be increased and a-axis to be contracted so the structure becomes tetragonal, i.e., ………. ………………………………………. , bct. The Martenisitic Phase in Steels

  18. The tetragonality, ie., the c/a ratio, of the bct cell of the martensite phase is governed by the carbon concentration. For a steel of composition x wt% C, a linear dependency gives the following relationships. The ………………………………….. of austenite are given by a = 0.3555 + 0.0044x The lattice parameters of martensite are given by a = 0.2866 – 0.0013x c = 0.2866 + 0.0106x Lattice Parameters of Austenite and Martensite

  19. Relationship between the Crystal Structures of Austenite and Martensite The a lattice parameter of the tetragonal martensite unit cell is given by While the c lattice parameter of the tetragonal martensite unit cell is given by

  20. Using the equations for the lattice parameter of austenite and martensite, the volumes of the units cells of the two tetragonal structures can be compared at a common carbon concentration, e.g., 1 %C. Hence, volume of austenite tetragonal cell, Vat Volume Changes Accompanying Martensite Formation Volume of martensite tetragonal cell, Vmt The increase in volume due to martensite transformation If this volume change is assumed to be isotropic because of the different orientations of the martensitic plates, then the associated linear expansion is given by 4.0/3 = 1.3% The relaxation of the c/a of martensite during tempering due to the reduction of carbon content caused by the carbide precipitation can thus create ………………………………………………. .

  21. When we look at the surfaces of these materials using optical microscopy, we see lines which appear as scratches. The scratches are continuous but change direction at the interface between the austenite and martensite phases Surface Relief Effects Surface relief effects in Fe-5%Pt

  22. These observations indicate that the surface is tilted in the region of the coherent interface so that the surface relief is of the form associated with a mechanical ……………… as opposed to ……………… deformation. Surface Relief Effects

  23. Lath martensite occurs in plain carbon steels with < 0.4% C and Fe-Ni-Mn. Lath Martensite Optical micrograph showing surface relief of ……………………. in F-0.2% C steel. Note: • The laths are typically 0.3 x 4 x 200 mm3. • The habit plane of this type of martensite is close to (111)g • The laths are usually observed in packets within which each adjacent lath has the same habit plane variant and shape deformation in contrast to lenticular martensites.

  24. These martensites occurs in high carbon steels with > 0.4% C and Fe-Ni-Mn, Fe, and Pt. Lenticular Martensites Optical micrograph showing surface relief of F-25% Pt alloy. The plates have the shape of a convex lens. This is confirmed by examination of successive sections after repeated removal of a thin surface layer of the sample. Since the interface planes are curved, the …………………. is taken as the plane of the centre-line of the plate or the “mid-rib”. More than one ……………….. of the habit plane may be observed within a single austenite grain, which gives different contrast of the light and dark plates. The martensite plates generally extend across a prior austenite grain and narrow to a point at the grain boundaries. Small martensite plates also form between larger prior-formed plates and extend across the available length between the prior plates.

  25. A minimum of 0.4% C is required to obtain significant hardness. At carbon contents of < 0.6%, the hardness of martensite decreases progressively with carbon content. See plot next page. At carbon contents of > 0.6%, the hardness plots flatten out and there is more experimental scatter. This is caused by increasing amounts of retained austenite in the steels so that the measured hardness is not truly indicative of 100% martensite. Effect of Carbon Content on Hardness of Martensite

  26. Effect of Carbon Content on Hardness of Martensite

  27. The hardness of martensite is determined ………………… by its carbon content because the interstitial carbon atoms: • Distort the bcc a-Fe structure to bct and thereby build up large elastic stresses, • Are very efficient at locking dislocations in place or ……………………. , which is responsible for the sharp yield point in a-Fe Substitutional alloying elements, such as Ni, Cr, Pt, etc, do not effect the hardness of martensite because: • They do not contribute to the tetragonality of the structure • As point defects they are not very efficient at locking dislocations Hence low alloy steels contain < 5% total alloy content. The hardness of 50/50 P/M can be predicted from the carbon content, which is usually taken as Rockwell C54. Effect of Alloying Elements on Hardness of Martensite

  28. The full diagram for a eutectoid steel shows: • The start and finishing times for isothermal pearlite and bainite reactions • The start and finishing temperatures for athermal martensite formation In this diagram, the temperature of the pearlite and bainite reactions ………… so the transition from pearlite to bainite is smooth and continuous. The Complete TTT Diagram for a Eutectoid Steel Above 550 oC, austenite transforms completely to pearlite Between 450-550 oC, both pearlite and bainite are formed Between 450 and 210 oC (the Ms), only bainite is formed On cooling below Ms, martensite is formed but in addition lower bainite can also form after long holding times.

  29. Path 1 Quench to 160 oC, hold for 20 min and then quench to RT. The pearlite transformation is suppressed by the quench. 50% martensite is formed at 160 oC but the holding time is not long enough to form bainite so more martensite is formed from 160 oC to RT. Path 2 Quench to 250 oC and hold for 100 sec, then quench to RT. The holding time at 250 oC is not long enough to form bainite so the austenite transform to martensite on cooling from 250 oC to RT. Microstructures from Various Time-Temperature Paths Path 3 Quench to 300 oC, hold for 500 s and quench to RT. The holding time at 500 oC produces 50% bainite with the remaining austenite tranforming to martensite on cooling to RT. Path 4 – Quench to 600 oC, hold for 104 s and quench to RT. 100% pearlite forms after 8 s at 600 oC with the additional holding time causing no further changes.

  30. In general, As the transformation temperature is ………………, a finer microstructure is …………………., which causes the tensile strength to be ………………. , while the ductility is …………………… . Effect of Transformation Temperature on the Mechanical Properties of a Eutectoid Steel