1 / 10

Collège Français des Biomatériaux Dentaires, Nancy, 2005

Sandblasting effect on flexural properties of fiber posts Effet du Microsablage sur le comportement en flexion des tenons fibrés. Collège Français des Biomatériaux Dentaires, Nancy, 2005. N.CHELEUX 1 & P. SHARROCK 2.

marny-cain
Download Presentation

Collège Français des Biomatériaux Dentaires, Nancy, 2005

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Sandblasting effect on flexural properties of fiber postsEffet du Microsablage sur le comportement en flexion des tenons fibrés Collège Français des Biomatériaux Dentaires, Nancy, 2005 N.CHELEUX1 & P. SHARROCK2 1 : Laboratoire d’Ecosystème Buccal et Biomatériaux, UPS Toulouse III, Fr. 2 : Laboratoire de Chimie Bio-inorganique Médicale, UPS Toulouse III, Fr.

  2. INTRODUCTIONMAT&METH RESULTATS DISCUSSION&CCL • Microsablage : • Répandu • Ruguosité • Surface de collage • Nergiz I, Schmage P, Platzer U, McMullan-Vogel : Effect of different surface textures on retentive strength of tapered posts.J Prosthet Dent. 1997 Nov;78(5):451-7. • Purton DG, Love RM, Chandler NP : Rigidity and retention of ceramic root canal posts.Oper Dent. 2000 May-Jun;25(3):223-7. • Sahafi A, Peutzfeldt A, Asmussen E, Gotfredsen K : Effect of surface treatment of prefabricated posts on bonding of resin cement.Oper Dent. 2004 Jan-Feb;29(1):60-8. • Sahafi A, Peutzfeldt A, Asmussen E, Gotfredsen K : Bond strength of resin cement to dentin and to surface-treated posts of titanium alloy, glass fiber, and zirconia.J Adhes Dent. 2003 Summer;5(2):153-62. • Sahafi A, Peutzfeldt A, Asmussen E, Gotfredsen K : Retention and failure morphology of prefabricated posts.Int J Prosthodont. 2004 May-Jun;17(3):307-12.

  3. v : 1 mm/min INTRODUCTIONMAT&METH RESULTATS DISCUSSION&CCL Essais de résistance au cisaillement (test de push-out) 20 à 40% Partie mâle (tenon) et femelle vue aérienne échantillon

  4. INTRODUCTION MAT&METH RESULTAT DISCUSSION&CCL Caractéristiques des tenons Conditionnement de surface par Microsablage des tenons • Microsableuse Dento-Prep (Ronvig, Danemark) • Particules d’alumine de 50 µ • 4 bars de P° • Perpendiculaire à la surf du tenon • Distance 20 mm • Pendant 10 sec

  5. F d F= Force (N) ; Iv = Portée (mm) ; L= long du tenon; d = Diamètre (mm) Iv L INTRODUCTIONMAT&METH RESULTATS DISCUSSION&CCL Dispositif d’essai Test de flexion 3 points : - Résistance à la contrainte maximale : σ (MPa) - Module d’élasticité axial : Ex (GPa) σ = 8 FMax l / πd3 Ex = S4l3/3πd4 L. Lassila, (2004) Dent Mater 20 (1):29-36. 1mm/min Fig 1 : Synergie 2000 MTS (Eden Prarie, USA) équipée du logiciel TestWorks 4.0.

  6. INTRODUCTIONMAT&METH RESULTATS DISCUSSION&CCL Résistance à la Contrainte Maximale Mpa NS NS NS NS Anova Test t de student

  7. INTRODUCTIONMAT&METH RESULTATS DISCUSSION&CCL Module d’Élasticité Axial Gpa NS NS NS NS Anova Test t de student

  8. INTRODUCTION MAT&METH RESULTATS DISCUSSION&CCL • Au cours des essais, trois modes de rupture peuvent se produire, l’essai n’est valable que si la rupture intervient en traction sur la face tendue inférieure ou en compression sur la face comprimée supérieure. • Les modes de rupture en cisaillement sont à exclure.

  9. INTRODUCTION MAT&METH RESULTATS DISCUSSION&CCL • Le Microsablage ne modifie pas le comportement en flexion des tenons • Forte liaison entre les fibres et la matrice • Haut degré de conversion de la matrice • Le module de flexion des tenons en fibre de verre est proche de celui de la dentine à l’inverse des tenons carbone (Rovatti, 1998 ; Drummond, 2000) • Le % de fibres, le type de fibre et de matrice • Radio-opacifiant, • Défauts internes ou de surfaces • Mauvaise liaison entre la fibre et la matrice (Asmussen, 1999 ; Ferrari, 2002 ; Drummond, 2003).