An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Elektrikdan SIFAT DIELEKTRIK LISTRIK DARI POLYANILINE –aL2o3 nanocomposite YANG BERASAL DARI BERBAGAI Al2O3 NANOSTRUKTUR(Adopt from : Journal Materials Chemistry, Author : Jiahua Zhu, Suying Wei, Lei Zhang, Yuanbing Mao, JongeunRyu, Neel Haldolaarachchige, David P. Younge and ZhanhuGuo) KAMI HARTATI-SEPTI APRILIA-TRI RAHAYU RPH Oleh :

  2. Proses hidrotermal yang diikuti oleh proses dehidrasi Empat nanostruktur: disintesis selanjutnya Polyaniline (PANI) menggabungkan keempat nanostruktur yang dibuat dengan metode SIP

  3. .

  4. Bahan

  5. Sintesis dari nanofiber

  6. Sintesis dari nanoplatet

  7. Sintesis dari nanorod

  8. Sintesis dari nanorod Sintesisdarinanoflake

  9. keempat sampel dipersiapkan untuk di calcined pada suhu 600oC selama 3 jam proseshidrotermalpadananostruktur keempat Al2O3 Nanostructures

  10. Sintesis PANI/Al2O3 nanocomposite

  11. .Karakteristik • TEM dan SEM • Analisis FT-IR • Analisis XRD • Daya Konduksi Elektrik • Daya Dielektrik • Analisis Termogavimetri • Differential scanning calorimetry (DSC) • Mekanisme SIP

  12. Hasil Analisis TEM

  13. Hasil Analisis FT-IR

  14. Hasil Analisis XRD

  15. Hasil Analisis TEM

  16. Hasil Daya Konduksi elektrik

  17. Hasil Daya dielektrik

  18. Hasil Analisis Termogavimetri

  19. Hasil • Differential scanning calorimetry (DSC)

  20. Hasil • Mekanisme SIP

  21. Kesimpulan • Al2O3 nanostructures telah berhasil disintesis melalui prosedur hydrothermal diikuti dengan satu proses dehidrasi. Selanjutnya, Polyaniline (PANI) nanocomposite menggabungkan keempat Al2O3 nanostruktur yang dibuat dengan menggunakan metode Surface Initialized Polymerization (SIP). • Struktur kristal dari PANI dipengaruhi oleh bentuk struktur nano Al2O3 dan bentuk morfologinya. • Daya konduksi elektrik dan dielektrik dari PNCs relatif kuat pada bentuk morfologi dan kualitas nanofillers. • Daya hambat PANI murni dan PANI / Al2O3 PNCs pada variabel 3-d dipengaruhioleh suhu. • Pada (VRH) menunjukkan mekanisme transportasi elektron. Peningkatan stabilitas termal dari PANI / Al2O3 PNCs menunjukkan kekuatan interaksi antara matrik polimer dan nanofiller melalui analisis DSC.