Volpe The National Transportation Systems Center. Finite Element Analysis of Wood and Concrete Crossties Subjected to Direct Rail Seat Pressure. U.S. Department of Transportation Research and Innovative Technology Administration John A. Volpe National Transportation Systems Center.

Download Presentation

Volpe The National Transportation Systems Center

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. VolpeThe National Transportation Systems Center Finite Element Analysis of Wood and Concrete Crossties Subjected to Direct Rail Seat Pressure U.S. Department of Transportation Research and Innovative Technology Administration John A. Volpe National Transportation Systems Center Hailing Yu and David Jeong Structures and Dynamics Division VolpeThe National Transportation Systems Center Advancing transportation innovation for the public good

  2. Overview • Background • Finite element analyses • Results • Conclusions • Future work • Acknowledgements

  3. Background • Rail seat failure in ties can cause rail rollover derailments • Plate cutting in wood ties • Rail seat deterioration in concrete ties • Probable cause for two Amtrak derailment accidents in Washington in 2005 and 2006 • Recently observed on the Northeast Corridor • Correlation of rail seat failure with rail seat load is needed

  4. Objectives • Develop finite element (FE) models for wood and concrete ties in a ballasted track • Study failure mechanisms of railroad ties subjected to rail seat loading using the FE models

  5. Current Simplifications • Fasteners are not modeled • Vertical load is applied as direct rail seat pressure • Lateral load is not applied

  6. Directionality in Wood Material R T L L: parallel to fiber T: perpendicular to fiber and tangent to growth rings R: normal to growth rings

  7. Orthotropic Elasticity

  8. Orthotropic Strength Limits

  9. Representative Wood Properties Based on properties of the white oak species described in Bergman, R., et al., “Wood handbook - Wood as an engineering material,” General Technical Report FPL-GTR-190, U.S. Department of Agriculture, Forest Service, Forest Products Laboratory: 508 p. 2010.

  10. Macroscopic Heterogeneity and Material Nonlinearity in Concrete Ties • Steel strands/wires • Linear elasticity with perfectly plastic yield strength • Concrete • Linear elasticity followed by damaged plasticity • Interfaces • Bond-slip depicted in linear elasticity followed by initiation and evolution of damage to bond

  11. Quarter Symmetric FE Models of 8-Strand and 24-Wire Concrete Crossties

  12. Concrete Material Models • Concrete damaged plasticity • Uniaxial tension: linear elasticity followed by tension stiffening • Uniaxial compression: linear elasticity followed first by strain hardening and then by strain softening • Multi-axial yield function • dt – tensile damage variable dc – compressive damage variable d – stiffness degradation variable (a function of dt and dc)

  13. Cohesive Interface Elements n – normal direction s, t – shear directions Normal traction tn Shear tractions ts, tt Quadratic nominal stress criterion for damage initiation

  14. Support to the Ties • Ballast • Extended Drucker-Prager model for granular, frictional materials • Subgrade • Modeled as an elastic half space using infinite elements • Transitional layers can be modeled if geometric and material properties are known

  15. Material Parameters • All material parameters are obtained from open literature • There is insufficient data on the bond-slip properties of steel tendon-concrete interfaces

  16. Analysis Steps • Initial condition • Steel tendons pretensioned to requirements (concrete tie) • First step (static analysis) • Pretension released in the tendons (concrete tie) • Second step (dynamic analysis) • Uniformly distributed pressure loads applied on rail seats (wood and concrete ties)

  17. Deformed Concrete Tie Shape After Pretension Release

  18. Compressive Stress State in Concrete After Pretension Release

  19. Ratio of Pretension Retention

  20. Wood tie – compressive rail seat failure Predicted Failure Mode Under Rail Seat Pressure

  21. Concrete tie – tensile cracking at tie base Predicted Failure Mode Under Rail Seat Pressure

  22. Rail Seat Force vs. Displacement Up To Predicted Failure Absolute rail seat displacement Rail seat displacement relative to tie base

  23. Partition of Tie-Ballast Interface • Fifty-one sub-surfaces on lower surface of wood tie • Contact force calculated on each sub-surface

  24. Contact Force Distribution on the Lower Surface of Wood Tie

  25. Conclusions • FE analyses predict that under a uniform rail seat pressure load, • The wood tie fails at the rail seats due to excessive compressive stresses • Tensile cracks form at the base of the concrete ties • The simplified loading application predicts rail seat failure in the wood tie but not in the concrete ties

  26. Future Work • Calibrate bond-slip relations in the steel tendon-concrete interfaces from tensioned or untensioned pullout tests • Incorporate fasteners and rails, and apply both vertical and lateral loading

  27. Acknowledgements • The Track Research Division in the Office of Research and Development of Federal Railroad Administration sponsored this research. • Technical discussions with Mr. Michael Coltman, Dr. Ted Sussmann and Mr. John Choros are gratefully acknowledged.