An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. PERTIMBANGAN PEMPROSESAN(PROCESSING CONSIDERATION)

  2. PLASTIK KONVENSIONAL BOLEH DI DAPATI DALAM PELBAGAI BENTUK SEPERTI KEPINGAN, I-BEAM, T-BEAM DAN BENTUK LAIN YANG MUDAH ATAU KOMPLEKS • NAMUN PRODUK PLASTIK MEMPUNYAI KELEBIHAN DARI SEGI PEMPROSESAN KERANA IA BOLEH DIHASILKAN DENGAN PELBAGAI BENTUK RUMIT YANG TIDAK MUNGKIN DIHASILKAN JIKA MENGGUNAKAN BAHAN LAIN

  3. PRODUK INDIVIDU BOLEH DIGABUNGKAN DENGAN BAHAGIAN YANG LAIN DENGAN MUDAH • OLEH KERANA KEPELBAGAIAN INI DAN DIGABUNGKAN DENGAN SIFAT-SIFAT FIZIKAL YANG BAIK, BANYAK KOMPONEN YANG DIHASILKAN DENGAN LOGAM TELAH DIGANTIKAN OLEH BAHAN PLASTIK, CONTOHNYA BUMPER KERETA, KOMPONEN KAPALTERBANG

  4. PEMILIHAN PROSES/TEKNIK FABRIKASI BERGANTUNG PADA: • SIFAT DAN KEPERLUAN SESUATU BAHAN MENTAH YANG DIGUNAKAN • SIFAT-SIFAT DAN BENTUK YANG DIPERLUKAN UNTUK PRODUK AKHIR • KOS, KELAJUAN DAN BILANGAN ATAU JUMLAH KESELURUHAN PRODUK YANG AKAN DIHASILKAN

  5. BUKAN SEMUA TEKNIK PEMPROSESAN SESUAI UNTUK SEMUA JENIS PLASTIK • PROSES FABRIKASI AKAN MEMPENGARUHI SIFAT-SIFAT STRUKTUR PLASTIK ATAU KOMPOSIT DAN RUPABENTUK PRODUK YANG DIHASILKAN

  6. PENGUJIAN DAN KAWALAN MUTU • UNTUK TERMOPLASTIK: SUHU PEMPROSESAN DAN KAEDAH PENYEJUKAN, TEKANAN, BENTUK PENGALIRAN LEBURAN PLASTIK, ‘KNIT LINES’, BAHAN TAMBAH DAN BAHAN BANTU PEMPROSESAN, KANDUNGAN LEMBAPAN DALAM BAHAN MENTAH, ‘STRESS’ DALAM PRODUK (CONTOH: REKABENTUK ACUAN, DAI) DAN JUGA PENARIKAN DAN REGANGAN PERLU DIBERIKAN PERHATIAN.

  7. UNTUK TERMOSET: KOMPOSIT ATAU PLASTIK DIPERKUATKAN: KESAN AGEN PENGKUPEL, BAHAN TAMBAH, KATALIS, KAEDAH PENEKANAN LAMINAT, CARA MENGELUARKAN RONGGA ATAU UDARA, CARA MELETAKKAN LAPISAN LAMINAT, KAEDAH DAN BENTUK ‘SPRAY-UP’ DAN JUGA PENYAMBUNGAN ADALAH SANGAT PENTING

  8. SIFAT-SIFAT PLASTIK YANG BIASA DIKAJI: • MEKANIKAL – TENSIL, HENTAMAN, PELENTURAN • KIMIA – KETAHANAN TERHADAP BAHAN KIMIA • ELEKTRIKAL – KEKONDUKSIAN, RINTANGAN, ANTI-STATIK • TERMAL – PENCUACAAN, PENGECUTAN, SUHU DEGRADASI • OPTIKAL – KECERAHAN, PENEMBUSAN CAHAYA • LAIN ??

  9. PIAWAIAN YANG BIASA DIGUNAKAN UNTUK UJIAN-UJIAN TERHADAP PLASTIK: • AMERICAN SOCIETY FOR TESTING AND MATERIALS (ASTM) • AMERICAN NATIONAL STANDARD INSTITUTE (ANSI) • INTERNATIONAL STANDARDIZATION ORGANIZATION (ISO) • PIAWAIAN MALAYSIA (MS) • SUPPLIERS OF ADVANCED COMPOSITE MATERIALS ASSOCIATION (SACMA) • PIAWAIAN GERMAN (DIN)

  10. PIAWAIAN BRITISH (BS) • UNDERWRITER’S LABORATORY (UL) • NATIONAL FIRE PROTECTION ASSOCIATION (NFPA) • NATIONAL ELECTRICAL MANUFACTURERS’ ASSOCIATION (NEMA) • PIAWAIAN LAIN (PENGELUAR KERETA – SAE, DSM) • PIAWAIAN SENDIRI

  11. CONTOH PIAWAIAN • ASTM 1897 (1972) – injection molding test specimens of TP molding and extrusion materials • ISO 868 (1978) – plastic hardness • BS 2782 (1978) – bending test • ASTM 790 (1971) – bending test • DIN 53453 (1975) – Charpy impact strength