An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 第十八章 镧系和锕系元素

  2. 主要内容 • 镧系、锕系元素通性 • 2. 我国稀土元素资源和提取 • 3. 核反应类型

  3. 18-1 镧系和锕系元素概述 镧系元素简写为Ln

  4. 18-1-1价层电子构型和氧化数 镧系元素的电子层结构最外层和次外层基本相同，只是4f上电子数不同，因而性质十分相似

  5. 氧化数的变化分为两个周期 La→Gd、Gd→Lu

  6. 18-1-2原子半径、离子半径和镧系收缩

  7. 210 200 190 180 170 Eu 原子半径/pm Yb 原子序数 镧系收缩——原子半径(总趋势)随原子序数的增加而缓慢减小的现象

  8. 双峰效应——原子半径在Eu、Yb处出现 　　　　　　骤升的现象。

  9. 双峰效应——熔点在Eu、Yb处出现 　　　　　　骤降的现象。

  10. 4200 4000 3800 3600 3400 ∑(I1+I2+I3)/(kJ·mol-1) 原子序数 双峰效应——第一、二、三电离能在 Eu、Yb处出现骤升的现象。

  11. 105 100 95 90 85 80 75 Ln3+半径/pm 原子序数 离子半径随原子序数的增加而缓慢减小

  12. 18-1-3 金属活泼性

  13. 均为活泼金属，仅次于碱金属，与镁接近。 在不太高的温度下, 可与氧、硫、氯、氮反应，可作脱硫剂、脱氧剂等。 可与水、酸反应，应将其保存在煤油里。

  14. 18-1-4 离子的颜色——呈周期性变化