Local Structural Properties of Magnetoresistive Materials

Local Structural Properties of Magnetoresistive Materials. G.I.L.D.A. Fabrizio Bardelli. Outline : Magneto-Resistive materials I - Manganites II - Double-Perovskites. r (H) - r (H=0) r (H=0). MR % = x 100. Magnetoresitive materials. Sr 2 FeMoO 6 300K.

kaspar
Download Presentation

Local Structural Properties of Magnetoresistive Materials

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Local Structural Properties of Magnetoresistive Materials G.I.L.D.A Fabrizio Bardelli Outline : Magneto-Resistive materials I - Manganites II - Double-Perovskites

  2. r(H) - r(H=0) r(H=0) MR% = x 100 Magnetoresitive materials Sr2FeMoO6 300K • Magnetoresistance (MR) : magnetization  resistivity • Conductive phase : • external applied magnetic field • magnetic order • Insulating phase : • high temperatures • paramagnetic phase Sr2FeMoO6 4.2K

  3. Interest in Manganites and Double-Perovskites • High Ferromagnetic Curie temperature (TC), • (up to 450 K in double-perovskites) • Half-Metallic Ferromagnetic (HMFM) ground state • electrical current is 100% spin polarized • TC can be raised by changing doping species and • concentration, pressure, magnetic field… • Manganites : prototype of strong electron • correlated systems • Double-perovskites : new mechanism at the origin • of magnetotransport properties Attractive both in terms of basic investigations and technological applications

  4. Magnetic storage technology : • MR materials have been used • for years in reading-heads • of hard disks • Future spintronic devices : • Spin-driven electronic • devices : • spin-valves • spin-injectors • tunnel junctions Technological applications Magnetic layer Magnetic layer Non-Magnetic layer Non-Magnetic layer Magnetic layer Magnetic layer Low resistance High resistance

  5. I Manganites Theory

  6. Doped manganites Chemical formula A1-x Bx MnO3 A = trivalent alkaline ion B = divalent rare earth Mn mixed valence : Perovskite cell O2- A = La3+, Y3+… B = Sr2+, Ca2+… Mn3+ Mn4+

  7. The Ca-doped series : La1-xCaxMnO3 • La3+ and Ca2+ are subsitutional • La1-xCaxMnO3 solid solution can be obtained with 0 ≤x ≤1 : LaMnO3CaMnO3 Mn3+ Mn4+ Jahn-Teller active ion Non Jahn-Teller active xCa Axially elongated octahedron Regular octahedron

  8. ferromagnetic conductive reduced distortion paramagnetic insulating enhanced distortion Magnetic transition (TC) Metal-to-Insulator transition (TMI) Structural transition (TS) (TC ~TMI ~TS) Local structure and magneto-transport properties M/Ms r (MW· cm) T (K) TC~ 260 K • Local structure : • Mn-O bond lengths • Mn-O-Mn bond angles

  9. First shell Radial distribution of atoms around the absorber |FT| (a.u.) Fourier Transform R(Å) Selective and local probe suitable to investigate the local structure around the absorber atom Extendend X-ray Absorption Spectroscopy (EXAFS) XANES valence state and geometry around absorber EXAFS coordination numbers (N) bond distances (R) local lattice distortions (s2) Absorption K-edge XANES EXAFS

  10. I Manganites Experimental

  11. Substrate affects the structure of thin films : Lattice mismatch asub-afilm afilm Substrates : STO = SrTiO3 (cubic 100) lattice mismatch = 0.5% NGO = NdGaO3 (cubic 110) lattice mismatch = -0.54% out-of-plane c 100x MR film MR film substrate STO substrate NGO a tensile stress compressive stress c < a c > a film-plane Sample thickness (Å) TC (K) c (Å) MR (%) 750 260 3.87 45 250 260 3.87 78 125 248 3.85 78 50insulating at any T La0.87Na0.13MnO3 PLD grown on STO substrate xNa= 0.13  Max. MR P.Ghigna, University of Pavia Na-doped manganite thin films Aim of this work is to study the evolution of the local structure as a function of the thickness

  12. TEY detector design goals: • Signal amplification • in gas phase • Low temperatures (down to 4.2 K) • Possibility to smear-out • eventual Bragg peaks • from the substrate ground to amplifier (1010) TEY current He2 e- X-rays polarized electrode insulating holders sample Challenging measurements : Total Electron Yield (TEY)detector Strong signal from the STO substrate prevented fluorescence acquisitions TEY has limited penetration depth => lower signal from the substate

  13. Still sample q d Oscillating sample Total Electron Yield (TEY)detector Incident beam Scattered beam Bragg condition: nl = 2sinq • oscillation period < 1s • Dqtheo»10-2rad • Dqexp < 1° +q Sample X-rays -q

  14. Mn-La Mn-Mn Mn-O Fourier transform First shell Average Mn-O bond lengths 50 Å RMnO(Å) 125 Å 250 Å 750 Å Increasing Mn-O distance with decreasing the film thickness EXAFS signal FIT EXAFS : results 750 Å 250 Å 125 Å 50 Å

  15. Mn-O bonds elongation 2% Strong static Jahn-Teller distortion of the MnO6 octahedra 50 Å film XANES pre-edge features A2 A1 An increased A1-A2 pre-edge peak splitting is the signature of a enhanced Jahn-Teller distortion (Elfimov et al.) Origin of the structural change : EXAFS : discussion Lattice Mismatch ? (0.5 %) Insulating behavior

  16. 2 x 2.07 Å 2 x 1.92 Å 2 x 2.07 Å 4 x 1.92 Å 50 Å film (insulating) RMn-O= 1.995 Å Bulk powder sample insulating phase RMn-O~ 1.98 Å JT JT Rexp.= 1.992 Film growth plane Reduction of the out-of-plane parameter (lattice mismatch) apical JT component constrained in the film growth plane EXAFS : discussion X-ray beam is polarized in the growth plane of the film We are sensitive only to in-plane bond distances !

  17. Thinnest film (50 Å) : • Fully strained structure • (dead-layer) Large Jahn-Teller distortion with apical component oriented in the plane of the film • Thicker films (250 and 750 Å): • Fully relaxed structure • (bulk values) As the structure relaxes there is no more a preferred orientation for the Jahn-Teller distortion Manganite thin films : conclusions • Intermediate thickness film (125 Å) : • Contributions from both fully strained ( ³ 40%) • and fully relaxed structures

  18. II Double-Perovskites Theory

  19. Sr2FeMoO6 : crystalline structure Double-perovskite cell Sr2+ Fe3+ Mo5+ O2- • Two interpenetrating FCC sublattices

  20. e-¯ Fe S=5/2 Mo Fe Mo S=1/2 Mo Fe Mo Fe Sr2FeMoO6 H(T) Mis-site disorder : Non perfect ordering of Fe and Mo ions Sr2FeMoO6 : mis-site disorder FM FM AFM Mis-site disorder reduces MR

  21. Sr2FeMoO6 - Half metallic ferromagnet - High Curie temperature - Large negative MR between 5 and 300 K Sr2FeWO6 - Insulating at all temperatures - Antiferromagnetic below 37 K xMo Mo ® W The W-doped series : Sr2FeMoxW1-xO6 • Subsituting Mo5+ with W6+ in Sr2FeMoO6 we obtain • the solid solution Sr2FeMoxW1-xO6 with 0 £x£1 • W-doping reduces the mis-site disorder rising TC A Metal to Insulator Transition (MIT) is expected at a certain value of x

  22. II Double-Perovskites Experimental

  23. Powder bulk samples (D.D.Sarma, Bangalore) : x = 0.0 Sr2FeWO6 x = 0.05 x = 0.15 x = 0.3 x = 0.6 x = 0.8 x = 1.0 Sr2FeMoO6 Sr2FeMoxW1-xO6 Resistivity measurements indicate a critical concentration (xc) in the interval 0.2 < xc < 0.3 Sr2FeMoxW1-xO6 samples Insulators MIT (xc~ 0.25) Conductors Aim of the work : Study of the evolution of the local structure as a function of the doping level

  24. Mo Fe O O O Fe O O O Sr O O O O O O O O Fe shell path deg. 1st RMo-ON = 6 O 1st RSr-O N=12 O O O EXAFS results Fe K-edge Mo Mo K-edge Mo Fe Mo W LIII-edge Sr K-edge Measured in transmission mode at 77K using Si 311 monocrhomator crystals

  25. XRD Sr-O XRD Fe-O XRD Mo/W-O • XRD data (Sanchez et al.) report a smooth evolution with x FM metallic EXAFS : first shell results AFM insulating FM metallic Fe-O AFM insulating Sr-O Mo-O W-O • Abrupt change in the local structure crossing xc • expansion of the FeO6 octahedra  Fe3+® Fe2+ • Contraption of MnO6 octahedra and of the Sr-O bonds

  26. XANES spectra : Fe and Mo K-edges insulating insulating x = 0.05 x = 0.0 x = 0.15 xc x = 0.05 xc x = 0.15 x = 0.3 x = 0.3 x = 0.6 x = 0.6 x = 0.8 x = 0.8 x = 1.0 x = 1.0 metallic metallic Energy (eV) Energy (eV) Huge and abrupt change of the charge distribution crossing xc Fe edge : change in the valence state (edge position) Mo edge : evidence of localization of the charge carrier in the insulating phase

  27. XANES spectra : W LIII- and Sr K-edges insulating insulating x = 0.0 x = 0.0 x = 0.05 x = 0.05 x = 0.15 x = 0.15 xc xc x = 0.3 x = 0.3 x = 0.6 x = 0.6 x = 0.8 x = 0.8 x = 1.0 metallic metallic W edge : No detectable changes, neither in the local structure nor in the valence state

  28. m(E) Fit x = 0.6 1.2 0.4 • Excess of the metallic Sr2FeMoO6 -like structure in the FM phase • The sistem does not change structure up to the critical concentration XANES : Fe edge considerations mfit(x) = a • mexp(Sr2FeMoO6) + (1 - a) • mexp(Sr2FeWO6) XANES spectra of doped compounds can be fitted by a linear combination of the two end compounds ( Sr2FeMoO6 - Sr2FeWO6 ) with a as fitting parameter.

  29. HMFM regionInsulating region 1. Valence transition Fe3+ Mo5+ W5+ Fe2+ Mo6+ W6+ 2. Percolative transition Mo5+®W6+ metallic Fe-Mo FM clusters connects each other permitting conduction Fe3+®Fe2+ FM Fe-Mo clusters are isolated by non magnetic Fe-W clusters Neither the valence transition nor the percolation scenario can describe the system ! Metal to Insulator Transition : two hypothesis (Kobayashi) XANES ®W does not change its valence state ! XANES ®excess of metallic/Sr2FeMoO6-like structure in the FM phase

  30. Double-perovskites : conclusions • EXAFS and XANES data depicts the microstructural • counterpart of the Metal to Insulator Transition • Contrary to XRD results we see an abrupt change of • the local structure crossing the critical concentration • XANES data show that neither the percolative • nor the valence transition are good models • to describe the system • More quantitative analisys is needed on the XANES • spectra

  31. Acknowledgements GILDA scientific group : Prof. S. Mobilio Dr. F. D'Acapito Dr. C. Maurizio M. Rovezzi Gilda technicians group: F. D'Anca F. Lamanna V. Sciarra V. Tullio Collaborators : C. Meneghini – University of "Roma Tre" P. Ghigna – University of Pavia D.D. Sarma – Bangalore Institute of Science

  32. Mo5+ S=1/2 Sr2FeMoO6 : kinetic driven mechanism (D.D. Sarma 2001) eg­ Fe3+ S=5/2 Ecry 4d1 Ecry eg¯ eg¯ Eex t2g­ t2g¯ Ecry 3d5 t2g¯ Eex EF t2g¯ eg­ Eex<Ecry Fe-Mo hybrid levels in presence of hopping interactions t2g­ Ecry Eex> Ecry AFM coupling between Mo delocalised and Fe localised electrons leads to FM coupling of the Fe sublattice

  33. Metallic phase Insulating phase Mo and W charge carriers belong to the Fe-Mo hybrid band Adding W changes neither the structure nor the charge distribution Below a critical concentration conduction band disappears due to the low level of Mo ions Charge carriers localize on Mo and Fe sites Charge localization induces a change of the Fe valence state (Fe3+® Fe2+) The greater ionic radius of Fe2+ drives the observed transition of the local structure

  34. Ground state is Semimetallic : • Up-spin : • gap at the • Fermi level (EF) • Down-spin : • finite DOS at EF Sr2FeMoO6 : ground state 1 O2p 0.5 eV Fe eg Fe eg Mo t2g Up Spin ­ EF Down Spin ¯ Mo/Fe t2g O2p 3.9 eV Up-spin states (­) : insulator Down-spin states (¯) : conductor Fully spin-polarized mobile charges !

  35. FM-MR conductive phase Temperaturevs doping phase diagram Doped manganites have complex phase diagram FM = FerroMagnetic AF = AntiFerromagnetic CAF = Canted AF FI = FM Insulator CO = Charge Ordered Maximum MR at x = 0.25 La1-xCaxMnO3 T(K) 350 300 250 200 150 100 50 0 paramagnetic insulating 0 0.2 0.4 0.6 0.8 1 xCa LaMnO3 CaMnO3

  36. eg s=1/2 q1 q2 eg s=1/2 q1 q2 t2g S = 3/2 t2g S = 3/2 Mn3+ O2- Mn4+ t2g S = 3/2 t2g S = 3/2 Y1 : Mn3+ - O2- - Mn4+ Mn4+ O2- Mn3+ Y2 : Mn4+ - O2- - Mn3+ Double-Exchange (Zener, 1951) Transport properties : antagonist mechanisms • Strong on-site • Hund coupling • Transfer integral • µ cos(q1- q2) Predicted Tc is too high ! Electron-phonon coupling(Millis, 1994 …forty years later !) Jahn-Teller polaron = charge carrier + Jahn-Teller lattice distortion Enhanced effective mass Þ reduced mobility

  37. XANES and EXAFS : • Abrupt change of the local structure crossing xc • System does not change adding W until xc is reached • W local structure does not change in the whole x range • XANES : • Excess of metallic/Sr2FeMoO6-like clusters in the FM phase • Evidences of charge localization on Mo and Fe sites in the AFM phase • W does not change valence ! • Valence state model predicts a change of the W valence state • Percolative model predicts Sr2FeMoO6andSr2FeWO6 changing in weight according to the nominal concentrations Summarising Neither the percolative nor the percolation scenario can describe the system !

  38. Mn O

  39. Double-Exchange (DE) vs Super-exchange (SE) SE : the interaction is mediated by virtual electron hoppings into unoppupied Mo d states vs DE : delocalised Mo 4d1 electron plays the role of the delocalised electron in manganites But : Localised up-spin band at Fe site is fully filled => Delocalised electron must be down-spin ! Therefore : Strong on-site Hund strenght, which couples FM localised and delocalised electrons in manganites, cannot be invoked in the case of double-perovkites Other mechanism ?

  40. Mn4+-site Mn3+-site dx2-y2 eg eg dz2 3d3 3d4 t2g t2g crystal field crystal field + Jahn-Teller Electronic levels Transport mechanism 1 • t2g Localised electrons form a core with S = 3/2 • eg conduction electron belongs to the Mn 3d – O 2p hybrid derived states • Strong on-site Hund strenght couples FM the localised and delocalised electrons

  41. 0.20 A2 A1 0.15 0.10 absorption 50 Å DE(A1 - A2) bulk 0.05 A2 A1 0.00 6536 6538 6540 6542 6544 Energy (eV) XANES eg DE(t2g - eg) t2g A1 A2 DE(A1 - A2) µDE(t2g - eg) Peaks splitting originates from the crystal field which is influenced by the Jahn-Teller distortion The large A1 – A2 energy splitting in the thinnest film is the signature of a large Jahn-Teller distortion