Structural Studies of Carbon Dust Samples Exposed to NSTX Plasma

Princeton University Geosciences. Structural Studies of Carbon Dust Samples Exposed to NSTX Plasma. Yevgeny Raitses and Charles H. Skinner Princeton Plasma Physics Laboratory Fuming Jiang and Thomas S. Duffy Department of Geosciences, Princeton University. May 26-30, 2008, Toledo, Spain.

iman
Download Presentation

Structural Studies of Carbon Dust Samples Exposed to NSTX Plasma

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. PrincetonUniversity Geosciences Structural Studies of Carbon Dust Samples Exposed to NSTX Plasma Yevgeny Raitses and Charles H. Skinner Princeton Plasma Physics Laboratory Fuming Jiang and Thomas S. Duffy Department of Geosciences, Princeton University May 26-30, 2008, Toledo, Spain 18th International Conference on Plasma Surface Interactions

  2. Abstract Raman analysis has shown that the production of carbon dust particles in NSTX involves strong modifications of the physical and chemical structure of the original graphite. Raman spectra were measured for different dust samples exposed to the NSTX plasma, unexposed dust samples, carbon deposits produced in an atmospheric pressure helium arc discharge, and heat-treated carbon samples. The arc electrodes and heat-treated samples were made from the same graphite material as the NSTX tiles. For the unexposed particles, the high energy G-mode peak (Raman shift ~1580 cm-1) is much stronger than the defect-induced D-mode peak (Raman shift ~ 1350 cm-1), a pattern that is consistent with Raman spectrum for commercial graphite materials. For dust particles exposed to the plasma, the ratio of G-mode to D-mode peaks is lower and becomes even less than 1. This behavior indicates on a strong increase of structural disordering in plasma exposed samples. We also demonstrate experimentally that heating to 1500-2500 C alone can not explain the observed structural modifications indicating that they must be due to higher temperatures needed for graphite vaporization, which is followed either by condensation or some plasma-induced processes leading to the formation of more disordered forms of carbon material than the original graphite. Moreover, because we found similar plasma-induced structural modifications in dust particles exposed under the different background gases (hydrogen and helium) and the different plasma conditions of the arc and NSTX experiments, our results suggest that the observed structural modifications can be unrelated to hydrocarbon compositions on the dust surface or implantation or thermal diffusion. This work was supported by the US DOE under contract No. DE-AC02-76CH03073

  3. Motivation • Dust from graphite tiles - tokamak safety issue. • Possible mechanisms of dust production: • Evaporation of wall material during disruptions etc. • Spallation and flaking of thin films or redeposited material. • Sputtering during wall cleaning or conditioning. • Plasma-induced synthesis and growth. • Different formation mechanisms of carbonaceous dust should leave their signatures in their macro and micro-structures.

  4. Results from previous dust studies • Raman spectroscopy studies suggest that tokamak-produced dustconsists of graphite-like particles with different degree of disordering.1,2 • Ion implantation,2,3 plasma-induced growth,4,5 heating3,6 etc may be responsible for the observed structural modifications of dust. Note: Similarities in structural modifications of carbon dust produced in JT-60 and by the low pressure (deuterium) arc discharge.7 1. P. Roubin et al.,J. Nucl. Mater. 337-339, 990 (2005) 2. T. Tanabe, “Application of optical techniques…”9th ITPA, Garching (2007) 3. K. Niwase et al., J. Nucl. Mater. 179-181, 214 (1991) 4. J. Winter, Plasma Phys. Control. Fusion 40, 1201 (1998) 5. Ph. Chappuis et al.,J. Nucl. Mater. 290-293, 245 (2001) 6. C. Arnas et al.,J. Nucl. Mater. 337-339, 69 (2006) 7. H. Yoshida et al., J. Nucl. Mater. 337-339, 604 (2005)

  5. Objectives and approach of this study • Explore plasma and thermal effects on structural modifications of graphite-type dust particles. • Compare Raman spectra from: • NSTX (deuterium discharge) • Atmospheric pressure helium arc discharge • Vacuum heat treatment (no plasma) • Unused graphite tile Note that we study carbon dust particles from very different plasma regimes, including pressure, gas and plasma properties.

  6. NSTX The National Spherical Torus Experiment (NSTX) research program is aimed at: • Exploring the physics of high beta and high confinement in a low aspect ratio device • Demonstrate non-inductive current generation and sustainment. • plasma major radius: 0.85 m, • minor radius: 0.68 m, • toroidal field of up to 0.55 T, • plasma current up to 1.5 MA • pulse duration up to 1.5 s. • 7 MW neutral beam injection • 6 MW of high harmonic fast wave RF at 30 MHz. Plasma facing components that are in contact with the plasma are protected by a combination of graphite and CFC tiles.

  7. Dust sampled by filtered vacuum collection technique (2001). NSTX dust (collaboration with Phil Sharpe INL.) SEM image of dust obtained from plasma-exposed surfaces in the upper divertor region of NSTX. Count based dust size distribution. Count median diameter 3.3 µm Composition: carbon, some particles also contain boron. J. P. Sharpe et al., J. Nucl. Mater, 337-339 (2005) 1000.

  8. Positioner Anode PPPL arc setup Graphite anode Brass cathode • Movable graphiteanode rod ( 0.5 cm) made from an unused NSTX tile and brass cathode disk ( 2.5 cm). • Arc chamber is evacuated by a vacuum pump and then filled to ~ 1 atm with Helium gas.

  9. Brass cathode Arc Graphite anode Soot deposit 1-2 mm Arc operation and heating experiments Typical arc parameters: Current : 80 A, Voltage: < 20 V Pressure: 1 atm (Helium) Anode temperature >3000 C Plasma: mostly carbon: • High heat flux from the plasma leads • to vaporization of a graphite anode. • Vapor products are deposited • on the cathode (anodic arc) Te ~ 1-5 eV Ti ~ 0.5 eV Ne ~ 1015/cm3 • Heating experiments: • Vacuum furnace (up to 1700 C) • Ohmic heating in arc setup • (1400-2000 C)

  10. 2 cm 0.1 cm Tip 2 cm 2 cm Examples of test samples used in this study NSTX flake and dust Post-run-arc cathode soot 0.1 cm Graphite sample used in heating experiments Post-run-arc anode

  11. Raman spectroscopy offers a sensitive measure of the microstructure of carbon dust Micro-Raman system* consists of An air-cooled 200 mW argon ion laser was operated at < 3 mW. holographic optics 0.5-m spectrometer Liquid nitrogen cooled CCD detector (1100 x 330 pixels). 0.2 W Ar laser Beam Splitter Dust Sample Depth of absorption (=514.5 nm) in graphite:~ 50 nm Spectrometer Energy level diagram Frequency shift of scattered light vibrational states Raman spectra contain information on vibrational energies, chemical bonds, molecular symmetry and the physical-chemical environment. *S.-H. Shim and T. S. Duffy, American Mineralogist 87, 318 (2002).

  12. Raman spectrum (RS) of carbon materials 1580 cm-1 1332  2 cm-1 Natural diamond Carbon nanotube (not found in NSTX) 1555 cm-1 Sample scraped from unused NSTX tile 1580 cm-1 G-mode • RS of graphite samples from the tile has 2 characteristic peaks: • Graphitelike G-mode (~1580 cm-1) • Disordered D-mode (~1350 cm-1) 1350 cm-1 D-mode

  13. Dust from NSTX: STRONG modifications Post-run dust samples • The peak intensities : ID/IG 1 indicate on strong disordering.1,2 • Similar Raman spectra for dust in Tore Supra3, JT-604. • also, for high energy irradiated • graphite samples5 and arc4. • Note:2 carbon black and glassy • carbon have RS with ID/IG > 1 Dust sample from unused graphite tile ID/IG 0.2 ID/IG 1.1 G-mode D-mode ID/IG 1.5 1. Tuinstra and Koenig, J. Chem. Phys. (1970) 2. R. Nemanich, S. Solin, Phys. Rev. B (1979) 3. P. Roubin et. al, J. Nucl. Mater. (2005) 4. H. Yoshida et al., J. Nucl. Mater. 2005) 5. K. Niwase et. al, J. Nucl. Mater. (1991)

  14. Arc-produced soot: STRONG modifications Post-run soot samples Brass cathode Dust sample from unused graphite tile ID/IG 1.15 ID/IG 0.2 Soot deposit 1580 cm-1 G-mode 1350 cm-1 D-mode Carbon ions, atoms and clusters from vaporized graphite anode reaching the brass cathode form a soot. ID/IG 0.8 Raman spectra of cathode soot and post-run NSTX dust samples are similar.

  15. Post-run anode tip: GRAPHITIC order Post-run samples from the anode tip Dust sample from unused graphite tile Graphite Anode Sample with thin deposit ID/IG 0.2 1580 cm-1 G-mode • In the arc operation, graphite anode is ablating: T > 3000C • Anode samples are essentially heat treated (T ~ 2500 C measured a few mm below the anode tip). • Post run anode has a thin film deposit on it. 1350 cm-1 D-mode without deposit (removed) ID/IG 0.2 Anode tip and NSTX dust samples have very different Raman spectra.

  16. Anode side Cathode side Hot part Heating experiments: WEAK disordering Vacuum furnace: Samples heated to 1700C at < 10-5 torr, for 1 hour Dust sample from unused graphite tile Ohmic heating (2000C) ID/IG 0.2 1580 cm-1 G-mode 1350 cm-1 D-mode Anode side ID/IG 0.1 Cathode side ID/IG 0.4 Thermal effects up to 2000 C alone do not lead to a strong disordering at temperatures insufficient for vaporization of the graphite

  17. Dust from Recent NSTX Experiments Preliminary Results • Samples were observed on a dust detector (P1-42) after retrieval from NSTX. • Similar to previous samples, the ratio ID/IG increases indicating on strong disordering. • Different Raman spectra in the range of 2800-3100 cm-1 . • Note that peaks in this range are usually assigned to heavier hydrocarbons involving C=C and C≡C bonds Dust sample from unused graphite tile ID/IG 0.7 ID/IG 0.2 G-mode D-mode 1. Ushizawa et al., Phys. Rev. B (1999). 2. D. Lin-Vien et al., Handbook of Infrared and Raman Characteristic Frequencies of Organic Molecules (Academic Press, Inc., 1991).

  18. Concluding remarks • Raman measurements indicate that the production of carbon dust particles in NSTX and arc discharge involves ablation processes (e.g. graphite vaporization), that are followed by the deposition and the formation of similarly disordered forms of carbon material.* Note: more disordered forms than the original graphite • The double peaked shape of the Raman spectrum of the NSTX dust and post-arc cathode soot is similar to the results from Tore Supra and JT-60. Note: this spectral shape is also found in highly disordered carbon black, and less disordered microcrystalline graphite and glassy carbon. • Higher resolution Raman measurements are required to investigate these structural similarities and to determine a more precise structure of the dust particles. * Y. Raitses, C. H. Skinner, F. Jiang, T. S. Duffy, “Raman spectroscopy of carbon dust samples from NSTX”, J. Nucl. Mater. 375 (2008), 365-369