PROCEDEE SPECIFICE METALURGIEI PULBERILOR PENTRU ELABORAREA PULBERILOR NANOSTRUCTURATE

PROCEDEE SPECIFICE METALURGIEI PULBERILOR PENTRU ELABORAREA PULBERILOR NANOSTRUCTURATE. MIHAIL MANGRA * , OANA GINGU * , GABRIELA SIMA * , ELISA RUIZ-NAVAS ** , ELENA GORDO ** , BEATRIX GOMEZ ** * Facultatea IMST, Universitatea din Craiova, Romania

hugh
Download Presentation

PROCEDEE SPECIFICE METALURGIEI PULBERILOR PENTRU ELABORAREA PULBERILOR NANOSTRUCTURATE

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. PROCEDEE SPECIFICE METALURGIEI PULBERILOR PENTRU ELABORAREA PULBERILOR NANOSTRUCTURATE MIHAIL MANGRA*, OANA GINGU*, GABRIELA SIMA*, ELISA RUIZ-NAVAS**, ELENA GORDO**, BEATRIX GOMEZ** *Facultatea IMST, Universitatea din Craiova, Romania Str. Calugareni, nr.1, cod 220037, Dr. Tr. Severin, www.imst.ro ** Departamentul de Stiinta si Ingineria Materialelor, Universitatea Carlos al III-lea din Madrid, Spania; www.uc3m.es A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  2. Compatibilitatea fizico-chimica dintre componentii compozitelor tip Al/SiC+Grafit Caracteristici ale compozitelor Al/SiC+Grafit • Raport favorabil dintre rezistenta mecanica (in special la uzare) si densitate • Stabilitate chimica si microstructurala la temperatura mediului ambiant si relativ ridicate (300-400)0C • Rezistenta la coroziune Aplicatii ale compozitelor tip Al/SiC+Grafit • Componente MEMS nanostructurate antifrictiune (sau de frictiune, in functie de alegerea componentilor compozitelor) A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  3. TEHNOLOGII DE ELABORARE a compozitelor nanostructurate Al/SiC+Grafit Alierea Mecanica Top-Down Bottom-Up A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  4. m 40 m 40mm MATERIALE ELABORATECompozite metalice usoare nanostructurate Al 2 h AM SiC 6 h AM aliere mecanica Grafit Al/SiC+5...10Gr A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie 10 h AM

  5. 2 horas 2 horas 6 horas 6 horas 100 100 10 horas 10 horas 90 90 80 80 70 70 60 60 % % 50 50 40 40 30 30 20 20 10 10 0 0 1 10 100 1000 1 10 100 1000 m m tamaño ( m) tamaño ( m) Al/20SiC+5Gr Al/20SiC+10Gr Variatia distributiei granulometrice a pulberilor nanostructurate functie de timpul de AM A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  6. 550 550 500 1,0 500 1,0 TDC 450 450 TDC e e 400 0,8 400 0,8 350 350 e ( %) 300 0,6 300 0,6 e TDC (A) TDC ( A) 250 250 (%) 200 0,4 200 0,4 150 150 100 0,2 100 0,2 50 50 0 0,0 0 0,0 2 4 6 8 10 2 4 6 8 10 Tiempo (h) Tiempo (h) Al/20SiC+5Gr Al/20SiC+10Gr Variatia marimii grauntilor cristalini functie de timpul de AM A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  7. 10 h 10 h 4500 5500 8 h 5000 8 h 4000 4500 6 h 6 h 3500 4 h 4000 3000 4 h 3500 2 h 2500 * 3000 counts 2 h counts 2000 2500 * 2000 1500 . . 1500 1000 * . . 1000 . . . . . . 500 . * . 500 * * * * * 0 h * 0 h 0 0 . 20 40 60 80 100 120 . 20 40 60 80 100 120 2q 2q Al SiC * Al * SiC Al/20SiC+5Gr Al/20SiC+10Gr Difractograme ale pulberilor nanostructurate elaborate prin AM A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  8. A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  9. Cuptor cu microunde comercial Regulator de temperatura Unitate de putere Unitate PC A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  10. Reprezentare schematica a montajului termocuplei A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  11. 100m 100nm b) a) Influenta materialelor initiale asupra structurii sinterizate MW Amestec de pulberi initiale Pulberi compozite nanostructurate Microstructuri reprezentative ale compozitelor nanostructurate sinterizate in microunde: 3000 C/15 min./racire lenta A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  12. 100nm 100nm Influenta temperaturii de sinterizare asupra structurii compozitelor nanostructurate hr = 450C/min; TMWS = 3000C; d = 15 min. hr = 450C/min; TMWS = 4000C; d = 15 min. Microstructuri ale Al/20SiCp+5Gr elaborate prin AM, sinterizate in MW in diferite conditii A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  13. 20 m 100nm Influenta variantei tehnologice de sinterizare asupra structurii compozitelor elaborate Structura compozitelor Al/20SiC+5Gr sinterizate clasic la parametrii: 7000C/ 6 h/racire lenta Structura compozitelor Al/20SiC+5Grsinterizate in MW la parametrii: 3000C/15 min/racire lenta A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  14. Proprietati ale compozitelor Al/SiC+5Gr sinterizate in MW *1: parametrii sinterizare MW: TMWS = 3000C; d = 15 min 2: parametrii sinterizare MW: TMWS = 4000C; d = 15 min 3: parametrii sinterizare MW: TMWS = 5500C; d = 20 min A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  15. Comparatie privind unele proprietatiale compozitelor sinterizate clasic respectiv MW A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  16. TESTAREA DE NANOINDENTARE A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  17. Diagrama tensiunilor Von Misses pentru ansamblul indentor-proba sinterizata Distributia deplasarilor pe aza Z pe structura compozita deformata A 5-a Editie a Seminarului National de Nanostiinta si Nanotehnologie

  18. Va multumim pentru atentie! Statuia lui Decebal, sculptata pe malul romanesc al Dunarii