Inconel Alloy 625 - Heanjia Super Metals Co Ltd

Inconel 625 prevents attack in alkalis, marine & fresh water and natural salts

Download Presentation

Inconel Alloy 625 - Heanjia Super Metals Co Ltd

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Nickel-Chrome Alloy Inconel 625 (UNS N06625) Inconel Alloy 625 is a corrosion and oxidation resistant nickel alloy that is employed for its high strength and good aqueous corrosion resistance properties. It prevents stress corrosion cracking due to chloride ions. It is resistant to pitting and crevice corrosion. Nickel 625 is a preferably used material in chemical processing, jet engines, aerospace and marine industry and nuclear power plants. Chemical Composition Carbon (C) 0.10 % Nickel (Ni) Rem % Chromium (Cr) 20 to 23 % Iron (Fe) 5 % Silicon (Si) 0.50 % Manganese (Mn) 0.50 % Sulfur (S) 0.015 % Phosphorous (P) 0.015 % Molybdenum (Mo) 8 to 10 % Titanium (Ti) 0.40 % Cobalt (Co) 1 % Niobium + Tantalum 3.15 to 4.15 % Aluminum (Al) 0.40 % Physical Properties Temperature oC 23 oC 100 oC 200 oC Electrical Resistivity Micro-ohm-meter 1.26 1.27 1.28 oF 74 oF 212 oF 392 oF Micro-ohm-inches 49.6 50 50.4 Heanjia Super-Metals Co., Ltd, Call- 12068907337. Web: www.super-metals.com

  2. 300 oC 400 oC 500 oC 600 oC 572 oF 1.30 oF 1.31 oF 1.32 oF 1.29 752 932 1112 50.8 51.2 51.6 52 Thermal Properties Temperature oC 23 oC 100 oC 200 oC 300 oC 400 oC 500 oC 600 oC Thermal conductivity W/M-°C 9.8 11.4 13.4 15.5 17.6 19.6 21.3 Thermal conductivity Btu-in./ft².-hr.-°F 68 79 93 108 122 136 148 oF 74 oF 212 oF 392 oF 572 oF 752 oF 932 oF 1112 oF Specific Heat Capacity Temperature oC 0 oC 100 oC 200 oC 300 oC 400 oC 500 oC 600 oC J/kg-°C Btu/lb-°F oF 32 oF 212 oF 392 oF 572 oF 752 oF 932 oF 1112 oF 429 446 463 480 496 513 560 0.102 0.107 0.111 0.115 0.118 0.123 0.134 Mena Coefficient of Thermal Expansion Temperatures oC 20 oC -204 oC 20 oC -316 oC 20 oC -427 oC 20 oC -538 oC 20 oC -649 oC 20 oC -760 oC 20 oC -871 oC 20 oC -982 oC x 10(-6)m/m-°C microinches/in.- oF 13.1 oF 13.5 oF 13.9 oF 14.4 oF 15.1 oF 15.7 oF 16.6 oF 17.3 oF 68-400 68-600 68-800 68-1000 68-1200 68-1400 68-1600 68-1800 7.3 7.5 7.7 8.0 8.4 8.7 9.2 9.6 Heanjia Super-Metals Co., Ltd, Call- 12068907337. Web: www.super-metals.com

  3. Mean Dynamic Modulus of Elasticity Alloy form Processing Temperature Average dynamic modulus of elasticity psi 30.2 x 10(6) psi 29,2 x 10(6) psi 28.8 x 10(6) psi 27.7 x 10(6) psi 26.7 x 10(6) psi 25.6 x 10(6) psi 24.3 x 10(6) psi 22.8 x 10(6) psi 21.2 x 10(6) psi 18.7 x 10(6) psi oF RT 200 oF 400 oF 600 oF 800 oF 1000 oF 1200 oF 1400 oF 1600 oF 1800 oF oC RT 93 oC 242 oC 316 oC 427 oC 538 oC 649 oC 760 oC 871 oC 982 oC Mpa 208,000 Mpa 201,000 Mpa 199,000 Mpa 191,000 Mpa 184,000 Mpa 176,000 Mpa 168,000 Mpa 157,000 Mpa 146,000 Mpa 129,000 Mpa Inconel 625 plate Annealed at 1925oF or 1052oC quickly quenched Corrosion Resistance 1.Creeping resistance 2.Oxidation resistance up to 1800oF 3.Resistance to seawater pitting and crevice corrosion 4.Prevents chloride ion stress corrosion cracking Average corrosion rate in Phosphoric acid Media temperature Test time days Mpy 42 days Corrosion rate oF 180 oF to 230 oF oC 82 oC to 110 oC Mm/a 0.04 Mm/a 28% wet process phosphoric acid (20% P2O5) 20-22% sulfuric acid, about 1-1.5% fluorideas fluosilicic acid. Aeration, moderate. Agitation, 55% wet process phosphoric acid (40% P2O5 equivalent containing 3% sulfuric acid and suspended calcium sulfate slurry. Aeration, none. Agitation, 50 ft/min (15 m/min) 99% wet process phosphoric acid (72% P2O5), 3.7% sulfuric acid (3% SO3), 0.5% fluoride. Aeration, moderate. Agitation Exhaust gases from evaporator, entrained phosphoric acid, sulfuric acid vapor, sulfur trioxide, nitrous acid, silicon tetrafluoride, water vapor; sprayed with water containing 0.1% phosphoric acid, 0.06% sulfuric acid, 0.1% combined fluoride. Aeration, extensive. Agitation, constantly sprayed with water Gases containing hydrofluoric acid, silicon fluoride sulfur dioxide with entrained phosphoric acid (72% P2O5), 3.7% sulfuric acid (3% SO3). Aeration, broad, Agitation, fast- moving gas stream 1.4 Mpy 230 oF to 234 oF 110 oC to 112 oC 112 days 59 Mpy 1.50 Mm/a 60 oF to 600 oF 50 oF to 355 oF 15 oC to 315 oC 10 oC to 180 oC 20.8 days 20.8 days 14.8 Mpy 12.9 Mpy 0.38 Mm/a 0.33 Mm/a 60 oF to 650 oF 15 oC to 343 oC 20.8 days 2.1 Mpy 0.05 Mm/a Heanjia Super-Metals Co., Ltd, Call- 12068907337. Web: www.super-metals.com

  4. Average Corrosion rate in salt containing conditions Media temperature Exposure time Corrosion rate Highest pitting depth Mill 1 Mill 40% calcium chloride, pH 2, 35% of time; 40% zinc sulfate pH 1.8, 35% of time; 3-30% aluminum sulfate, pH 3, 15% of time; 40% magnesium sulfate pH 3, 10% of time; 40% zinc chloride, pH 1.8 5% of time. Aeration, moderate. Agitation, lightnin’ mixer. Cuprous chloride, cuprous cyanide, p- chlorophenol-N-methyl pyrolidone, p- cyanophenol. Aeration, none. Agitation, by boiling only. 5-20% cyanuric chloride in carbon tetrachloride or toluene, 0.5% chlorine, 0.3% cyanogen chloride, hydrogen chloride and phosgene Zinc chloride up to 71% (72° Be). Aeration, none; under 28 in. (71 cm) vacuum. Agitation. 51% magnesium chloride, 1% sodium chloride, 1% potassium chloride, 2% lithium chloride as concentrated from natural Bonneville brines of 33% solubles. Aeration, little. Agitation, moderate. Liquid phase Vapor phase oF 70 oF to 200 oF oC 21 oC to 93 oC Mpy 0.1 Mpy Mm/a 0.003 Mm/a mm 0.03 mm 73 days 455 oF 235 oC 43 hours 0.5 Mpy 0.013 Mm/a - - - - - 0.5 Mpy 0.013 Mm/a 1 Mill 0.03 mm 255 oF 107 oC 35 days 0.3 Mpy 0.008 Mm/a 3 Mill 0.00 8 mm - - 330 oF to 335 oF 330 oF to 355oF 165 oC to 168 oC 165 to 180 100 h with brine only, 20 h with 0.2% fluosilicic acid and 0.1% HF 2 Mpy 3 Mpy 0.05 Mm/a 0.08 Mm/a - - - 53% magnesium chloride, 1% sodium chloride, 1% potassium chloride, 2% lithium chloride as concentrated from natural Bonneville brines of 33% solubles. Aeration, little. Agitation, moderate to considerable. Vapor phase above 53% magnesium chloride with 8,000-10,000 ppm hydrochloric acid in condensate. Aeration, air-free after start-up. 335 oF to 355 oF 168 oC to 180 oC 200 hours 0.5 Mpy 0.013 Mm/a - 335 oF to 345 oF 168 oC to 174 oC 200 hours 4 Mpy 0.10 - - Mm/a Heanjia Super-Metals Co., Ltd, Call- 12068907337. Web: www.super-metals.com

  5. Vapors over 50% magnesium chloride with 500-4000 ppm hydrochloric acid in condensate and 1000 ppm magnesium chloride. Aeration, moderate after start-up. Agitation. 50% magnesium chloride solution plus 1% sodium chloride, 1% potassium chloride, 2% lithium chloride, concentrating natural Bonneville brine from 33% soluables to 50%. Aeration, little. Agitation, moderate 310 oF 154 oC 45 hours 2 Mpy 0.05 Dispers ed pits Disp erse d pits Mm/a 310 oF 154 oC 45 hours 0.8 Mpy 0.020 Mm/a Dispers ed pits Disp erse d pits Mechanical Properties Impact Strength Aging temperature, oF, oC Annealed 1200 oF, 649 oC Aging period in hours Average charpy V notch impact strength Ft. lbs - 81 Ft. lbs 1000 11 Ft. lbs 4000 8 Ft. lbs 8000 5 Ft. lbs 16000 4 Ft. lbs 1000 5 Ft. lbs 4000 4 Ft. lbs 8000 5 Ft. lbs 16000 4 Ft. lbs 1000 12 Ft. lbs 4000 11 Ft. lbs 8000 15 Ft. lbs 16000 14 Ft. lbs J 110 J 15 J 11 J 7 J 5 J 7 J 5 J 7 J 5 J 16 J 15 J 20 J 19 J 1400 oF, 760 oC 1600 oF, 871 oC Hardness and tensile properties at Room temperature Condition Forms Ultimate tensile strength Ksi 0.2 % offset Yield strength Ksi Elongatio n % in 2 inches Hardne ss, rockwel l B94 Mpa Mpa Annealed at 1925oF or 1052oC, quickly quenched Annealed at 1925oF or 1052oC, quickly quenched Annealed at 1925oF or 1052oC, quickly quenched sheet 132 Ksi 910 Mpa 67.9 Ksi 468 Mpa 47 % sheet 131.5 Ksi 907 Mpa 67.4 Ksi 465 Mpa 45 % B97 Plate 0.25 inch 0.5 inch 0.75 inch 132 Ksi 130 Ksi 132.3 Ksi 910 Mpa 896 Mpa 912 Mpa 65.5 Ksi 67 Ksi 80 Ksi 452 Mpa 462 Mpa 552 Mpa 46 % 44 % 44 % B94 B98 B98 Heanjia Super-Metals Co., Ltd, Call- 12068907337. Web: www.super-metals.com

  6. 1 inch 1.5 inch 1.75 inch 127.2 Ksi 127.3 Ksi 128 Ksi Available Forms 877 Mpa 878 Mpa 883 Mpa 75.3 Ksi 73.7 Ksi 66 Ksi 519 Mpa 508 Mpa 455 Mpa 42 % 43 % 44 % B97 B97 C20 Wire, Wiremesh, Flanges, Tubing, Pipe, Strip, Plate, Foil, Sheet, Rod, Bar Heanjia Super-Metals Co., Ltd, Call- 12068907337. Web: www.super-metals.com