共析转变. 《 材料科学基础》 第八章第四节. 固态相变. 第四章第四节. Acm. A3. A1. 固态相变. 共析转变是奥氏体冷却到 A1 （ Ar1 ） 以下发生的相变.  （ 0.77%C)  (0.022%C) + Fe 3 C(6.69%C). P 为  和 Fe 3 C 成交替分布的片层状组织. P 转变包含两个过程： C 的扩散 和 晶体点阵重构. 珠光体 P. 索氏体. 650 － 600 ° C 下形成，片间距 400 － 200nm. 珠光体团. 屈氏体. 600 － 500 ° C 下形成，片间距 <200nm.

gyan
Download Presentation

固态相变

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 共析转变 《材料科学基础》第八章第四节 固态相变 第四章第四节

  2. Acm A3 A1 固态相变 共析转变是奥氏体冷却到A1（Ar1）以下发生的相变 （0.77%C)  (0.022%C) + Fe3C(6.69%C) P为和Fe3C成交替分布的片层状组织 P转变包含两个过程：C的扩散和晶体点阵重构

  3. 珠光体 P 索氏体 650－600°C下形成，片间距 400－200nm 珠光体团 屈氏体 600－500°C下形成，片间距 <200nm 片间距 固态相变

  4. 固态相变 一、珠光体的形成 1.形核 几乎都是晶界形核，非均匀形核 晶界处常富碳，Fe3C优先形核，消耗C，贫C区又促进形核，由此构成P核心。 在一个珠光体团中，  和Fe3C之间存在一定晶体学取向关系。

  5. t2 t1 C  C Fe3C C   C Fe3C 固态相变 2.长大

  6. u I 700°C 500°C T 固态相变 二、共析转变动力学 1. 形核率I和长大速率u

  7. A1 P B Ms 固态相变 2. 共析转变动力学图 共析转变特点： （1）孕育期 （2）转变最快温度和时间

  8. 先共析转变 亚共析钢或过共析钢分别降温到Ar3和Arcm以下温度时发生先共析相的析出。 伪共析转变 亚共析钢或过共析钢从奥氏体状态快速冷却到Ar1温度以下，先共析相来不及析出，奥氏体直接转变伪铁素体和渗碳体。 固态相变 三、先共析转变和伪共析转变