Bolted joint failure modes

Bolted joint failure modes. F. Matthews, in Handbook of Polymer Composites for Engineers. Lay-up 1: [+45,0,-45,0,90,0,+45,0,-45,0] s Lay-up 2: [+45,-45,0 2 ,+45,90,-45,0 3 ] s Lay-up 3: [+45,-45,+45,-45,90,0 5 ] s Lay-up 4: [+45,-45,0 2 ,90,0,+45,-45,0 2 ] s Lay-up 5:

dima
Download Presentation

Bolted joint failure modes

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Bolted joint failure modes F. Matthews, in Handbook of Polymer Composites for Engineers

  2. Lay-up 1: [+45,0,-45,0,90,0,+45,0,-45,0]s Lay-up 2: [+45,-45,02,+45,90,-45,03]s Lay-up 3: [+45,-45,+45,-45,90,05]s Lay-up 4: [+45,-45,02,90,0,+45,-45,02]s Lay-up 5: [+45,-45,05,+45,-45,90]s Effect of ‘blocked’ laminate stacking sequence on bearing strength

  3. Simplified procedures for designing composite bolted joints from CC Chamis, J Reinf Plast & Comp.,vol 9, pp614-626

  4. e w d laminate thickness = t Basic bolt geometry F y x

  5. 1. Bearing (compression) failure F At failure, F = d t sxc

  6. 2. Tension failure F At failure, F = (w-d) t sxT

  7. 3. Wedge splitting(due to lateral pressure of bolt) F/2 F At failure, F = ½(2e - d) t syT

  8. 4. Shear out F At failure, F = 2 e t txy

  9. 5. Combined tension and shear F At failure, F = ½ t [(w - d)sxT + 2 e txy]

  10. Example failure analysis High strength carbon/epoxy laminate. Layup [0,±45,0,90]s - 10 plies at 0.125 mm per ply. Fibre volume fraction: 60% Strength values: long. tension (sxT) = 546 MPa trans. tension (syT) = 343 MPa long. compression (syT) = 550 MPa in-plane shear (txy) = 267 MPa

  11. Example failure analysis Bolt diameter (d) = 6 mm Laminate thickness (t) = 1.25 mm Joint width, or bolt spacing (w) = 25 mm Edge distance (e) = 25 mm Applied load (F) = 5000 N

  12. 1. Bearing (compression) Compressive stress is sxc = F / d t = 5000 / (6 x 1.25) = 667 MPa This is greater than the compressive strength of the laminate, so bearing failure occurs. The maximum load would be 550 x 6 x 1.25 = 4125 N

  13. 2. Tension Tensile stress is sxT = F / (w - d) t = 5000 / (19 x 1.25) = 211 MPa This is less than the tensile strength of the laminate, by a factor of 2.6. And so on…each failure mode is considered separately, and a margin of safety calculated.

  14. Geometrical aspects It is straightforward to use a spreadsheet to examine the dependence of overall strength and failure mode on bolt geometry. The following example takes the laminate information given above, and calulates failure loads for the 5 different modes as a function of bolt diameter:

  15. - shear failure load is independent of bolt diameter- bearing failure occurs for d < 12 mm- strongest joint has d between 12 and 13 mm, where several failure modes are likely (for this laminate)

  16. Multi-bolt joints from CC Chamis, J Reinf Plast & Comp.,vol 9, pp614-626

  17. Example analysis of multi-bolt joint Connection required between composite panel and metal plate. Assume that all bolts share load equally. Bolts are ‘designed’ for the composite - we assume the metal plate is strong enough. High strength carbon/epoxy laminate, as defined previously.

  18. Example analysis of multi-bolt joint Design tensile load (P) = 400 N/mm Bolt diameter (d) = 6 mm Bolt spacing (p) = 6 bolt diameters = 36 mm Edge distance (e) = 4 bolt diameters = 24 mm

  19. Load carried per bolt F = bolt spacing x load per unit width = 36 mm x 400 N/mm = 14400 N = 14.4 kN

  20. Number of bolts per row 1. Assuming bearing failure mode: n = F / d t sxc = 14400 / (6 x 1.25 x 550) = 3.5 so 4 bolts are required to avoid bearing failure.

  21. Number of bolts per row 2. Assuming tension failure mode: n = F / (p - d) t sxT = 14400 / (36 - 6) x 1.25 x 546) = 0.7 so only 1 bolt is required to avoid tensile failure.

  22. Check other failure modes for edge and centre bolts 3. Check first row centre bolt in shear-out: Each bolt takes 14400 / 4 = 3600 N Shear stress = 3600 / (2 e t) = 60 MPa Compare with shear strength of laminate: 60 < 267 MPa, so OK.

  23. Check other failure modes for edge and centre bolts 4. Check first row centre bolt in wedge splitting: Transverse tensile stress = 2 x 3600 / [(2e - d) t] = 137 MPa Compare with transverse tensile strength of laminate: 137 < 343 MPa, so OK.

  24. Check other failure modes for edge and centre bolts 5. Check corner bolt in tension/shear-out: Force required to cause failure: F = ½ t [(p - d)sxT + 2 e txy] = 18248 N This is much greater than the actual load on this bolt (3600 N), so OK.

  25. Other factors not included in preliminary design: • Bypass load • Friction effects • Cyclic loading and laminate degradation • Thermal and moisture effects • Biaxial loads • Flat-wise compression