LDC borstplätering Tel: +46 248 17440 ldc@swipnet.se. Plating in the valveseat pockets for corrosion protection. LDC borstplätering. Cylinderhead exhaust seat pocket automatically Ni plated for corrosion protection. LDC borstplätering Tel: +46 248 17440 ldc@swipnet.se.

dee
Download Presentation

LDC borstplätering Tel: +46 248 17440 ldc@swipnet.se

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. LDC borstpläteringTel: +46 248 17440 ldc@swipnet.se • Plating in the valveseat pockets for corrosion protection. www.ldc-brushplating.com

  2. LDC borstplätering Cylinderhead exhaust seat pocket automatically Ni plated for corrosion protection www.ldc-brushplating.com

  3. LDC borstpläteringTel: +46 248 17440 ldc@swipnet.se • Damaged valvseats pocket are being repaired with copper to bring it back to size. www.ldc-brushplating.com

  4. LDC borstplätering • Copper plating is finished with a thickness of 1,5 mm. www.ldc-brushplating.com

  5. LDC borstplätering • Machining the copper back to nominal size. www.ldc-brushplating.com

  6. LDC borstplätering • Machining of the copper is now finished and ready for the final nickel capping. www.ldc-brushplating.com

  7. LDC borstplätering • Nickel plating is finished and the seat pocket is back in size again and an excellent corrosion protection is made to save the surface fore several years from new corrosion and plating is already started in the next pocket. www.ldc-brushplating.com

  8. LDC borstplätering • The test results Wärtsilä have done after Nickel plating is weary good, after 22k running hours it was no corrosion on the Nickel plated areas. www.ldc-brushplating.com