NANOINGINERIE APLICATA LA OBTINEREA UNOR MATERIALE REACTIVE
This presentation is the property of its rightful owner.
Sponsored Links
1 / 20

NANOINGINERIE APLICATA LA OBTINEREA UNOR MATERIALE REACTIVE E. S. Dragan, F. Bucatariu, M. Mihai PowerPoint PPT Presentation


  • 74 Views
  • Uploaded on
  • Presentation posted in: General

NANOINGINERIE APLICATA LA OBTINEREA UNOR MATERIALE REACTIVE E. S. Dragan, F. Bucatariu, M. Mihai Institutul de Chimie Macromoleculara “P. Poni”, Iasi E-mail: [email protected] Arhitecturi supramoleculare nanometrice realizate prin tehnici nedistructive si nepoluante.

Download Presentation

NANOINGINERIE APLICATA LA OBTINEREA UNOR MATERIALE REACTIVE E. S. Dragan, F. Bucatariu, M. Mihai

An Image/Link below is provided (as is) to download presentation

Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author.While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server.


- - - - - - - - - - - - - - - - - - - - - - - - - - E N D - - - - - - - - - - - - - - - - - - - - - - - - - -

Presentation Transcript


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

NANOINGINERIE APLICATA LA OBTINEREA UNOR MATERIALE REACTIVE

E. S. Dragan, F. Bucatariu, M. Mihai

Institutul de Chimie Macromoleculara “P. Poni”, Iasi

E-mail: [email protected]


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Arhitecturi supramoleculare nanometrice realizate prin tehnici nedistructive si nepoluante

Materiale hibride reactive realizate prin adsorbtia

strat-dupa-strat

a polielectrolitilor slabi pe microparticule de silice

Filme subtiri realizate prin adsorbtia

strat-dupa-strat

a poliionilor si compusilor mic-moleculari pe suprafete plane

Complecsi polielectrolitici nestoechiometrici ca dispersii coloidale stabile


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

STRUCTURILE POLIIONILOR

NaPAMPS

PDADMAC

p = 0.95, PCA5; p = 0.94, x = 9, PCA5D1


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

METODE UTILIZATE IN STUDIUL COMPLECSILOR POLIELECTROLITICI

Prepararea

Volume variabile de titrant ca solutie aposa s-au adaugat solutiei apoase de poliion de semn contrar, cu o viteza constanta cuprinsa in domeniul 0.1 – 1.5 mL/mL. h, cu agitare magnetica, la temperatura camerei (aprox. 25 oC).

Caracterizarea complexului interpolielectrolitic

Caracteristicile dispersiei de complex s-au urmarit prin: densitatea optica la  = 500 nm (OD500), masurata cu un spectrometru Lambda 900 UV/Vis (Perkin Elmer, United Kingdom), si prin difuzia dinamica a luminii la un aparat Zetasizer 3000 (Malvern Instruments Ltd, United Kingdom), la un unghi de difuzie de 90o si o lungime de unda de 633 nm. Dimensiunea medie a nanoparticulelor, Rh, si indicele de polidispersitate, PI, s-au evaluat automat printr-un program CONTIN.


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Influenta structurii policationului asupra caracteristicilor nanoparticulelor de complex la o viteza de adaugare a polianionului de0.28 mL NaPAMPS/mL PDADMAC.h

E. S. Dragan, S. Schwarz J. Polym. Sci.: Part A: Polym. Chem. 2004, 42, 2495.


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Influenta masei moleculare a polianionului asupra razei nanoparticulelor de complex la o viteza de adaugare de 0.28 mL NaPAMPS/mL PDADMAC.h

E. S. Dragan, S. Schwarz J. Polym. Sci.: Part A: Polym. Chem. 2004, 42, 2495.


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Influenta concentratiei poliionilor asupra caracteristicilor complexului la o viteza de adaugare de

0.28 mL NaPAMPS/mL PDADMAC.h


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Dimensiunea, Rh, si indicele de polidispersitate a nanoparticulelor de complex in functie de viteza de adaugare a NaPAMPS si de raportul intre sarcini


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

polianion

polication

(n-/n+)iso

+

complex primar

Reprezentarea schematica a influentei

vitezei de adaugare a titrantului asupra

nivelului de agregare a complexului


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

OD500 si dimensiunea particulelor, Rh,

in functie de viteza de adaugare a NaPAMPSla un raport n-/n+ de 1.2


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Stabilitatea coloidala la pastrare a dispersiei de

nanoparticule de complex in functie de raportul intre sarcini la o viteza de adaugare de 0.88 mL NaPAMPS/mL PCA5.h


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Test de floculare a silicei coloidale (200 nm) cu complecsi polielectrolitici nestoechiometrici comparativ cu policationii singuri (PCA5 si PCA5D1)


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Colorantii utilizati in constructia de filme subtiri multistrat nanostructurate;

policationul utilizat: PCA5

Direct Red 80 (DR80)

Direct Blue 1 (DB 1)

Crocein Scarlet MOO (CSMOO)

Ponceau SS (PSS)


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

PREZENTAREA SCHEMATICA A TEHNICII DE ADSORBTIE STRAT-DUPA-STRAT IN OBTINEREA DE FILME SUBTIRI PCA5/COLORANT AZOIC

Apa deionizata

Colorant in apa

Apa deionizata

PCA5 in apa


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Absorbanta la lungimea de unda caracteristica fiecarui colorant in functie de numarul de straturi


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Water, PCA5 10 mM,

Ra = 2.02 nm

1 M NaCl, PCA5 10 mM,

Ra = 3.44 nm

1M Na2SO4,PCA5 10 mM,

Ra = 2.72

1 M

1 M NaCl, PCA5 10 mM,

Ra = 2.31 nm


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Grosimea totala a filmului (PCA5/DR80)n si grosimea unei perechi de straturi pentru filmele construite prin adsorbtia policationului din solutii apoase de electrolit mic molecular masurate prin elipsometrie


Structurile polimerilor utilizati in obtinerea materialelor hibride reactive pe suport de silice

Structurile polimerilor utilizati inobtinereamaterialelor hibride reactive pe suport de silice

P(VAm-co-FA)

PAA

EDA

Mw= 40.000 g/mol

Mv= 68.000 g/mol


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

SCHEMA DE FORMARE A MATERIALULUI HIBRID


Nanoinginerie aplicata la obtinerea unor materiale reactive e s dragan f bucatariu m mihai

Potentialul Zeta functie de pH pentru materialul hibrid silice/(PVAm/PAA)n