1 / 14

膨胀石墨的改性

膨胀石墨的改性. 研究生：王娜 导师：那平 2012-11-3. 主要内容. 前期工作. 1. 遇到问题. 2. 3. 今后的思路. 4. 二、前期工作. 目前的思路 想法 :.

amiel
Download Presentation

膨胀石墨的改性

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 膨胀石墨的改性 研究生：王娜 导师：那平 2012-11-3

  2. 主要内容 前期工作 1 遇到问题 2 3 今后的思路 4

  3. 二、前期工作 目前的思路 想法: • 1.目前,油吸附材料主要有无机材料( 如膨胀石墨、 蛭石、 有机化黏土等)、 天然有机材料( 如稻草、 棉花、 亚麻和木棉纤维等)和合成聚合物材料(如聚丙烯、 聚苯乙烯、 聚乙烯和聚丙烯酸酯等)。 • 2.木棉纤维接枝聚苯乙烯吸油材料。对氯仿和甲苯的吸油倍率分别达到了65. 4 g/ g和43 . 2 g / g。该吸油材料有快速吸油能力, 在15 min 可达吸附平衡。 • 3.目前膨胀石墨接枝聚苯乙烯主要用在阻燃、导电、塑料泡沫等方面，未见用于水处理方面。

  4. 目前的思路 材料制备方法： 二、前期工作 1、先把EG氧化为EGO，然后制末端含羧基的聚苯乙烯。

  5. 目前的思路 材料制备方法： 二、前期工作 2、2gEG +70mlDMF +1.1g PS+0.045gBPO 3、 2gEGO +70mlDMF +1.1g PS+0.045gBPO 2gEG+70mlDMF

  6. 目前的思路 二、前期工作 材料表征：EGEG/PS红外光谱的分析

  7. 目前的思路 二、前期工作 材料表征：EGEG/PS红外光谱的分析

  8. 目前的思路 二、前期工作 吸油率的测定： 1、在烧杯中滴加油和EG/PS，搅拌，观察现象。

  9. 二、前期工作 目前的思路 吸油率的测定 2、分别加入等量的EG和EG/PS，移5ml，10ml, 15ml油，搅拌，观察现象。 5ml油和EG 5ml油和EG/PS 10ml油和EG 10ml油和EG/PS 结论：a、EG/PS的吸油率远 小于EG。 b、EG/PS团聚能力差。 15ml油和EG

  10. 二、遇到的问题 • 1.在反应聚合的过程中破坏了膨胀石墨的孔结构，导致孔径的坍塌，孔的比表面积 降低，以至于吸附减弱。 • 2.膨胀石墨接枝后，材料密度增大，在水体系中下沉，不利于表面油的吸附 。 • 3.膨胀石墨接枝后，并没有达到预期的在水体系中吸油后团聚的效果。

  11. 三、今后的思路 1、无机材料在膨胀石墨表面的改性（例如：纳米氢氧化镁）。 2、接枝其他的有机物（例如：凝油材料）。

  12. 一篇文献 由辛烯、苯乙烯、二乙烯基苯交联共聚形成的高分子材料（Oil Superabsorbent Polymer ，简写为Oil−SAP）。 特点（1）吸油率高，高达自身重量的45倍。 （2）只吸油，不吸水，吸油后形成一种凝胶漂浮在水面。 （3）吸油后，机械强度大，很容易打捞。 反应方程式

  13. 机械强度

  14. 谢 谢！