Fatigue Characteristic of RC Beams Strengthen with CFRP Strand sheet. B4 Junpei Kasai. Today’s Topic. ・ Background & Purpose ・ Experiment & Result ・ Future plan. Static behavior. Background & Purpose. clear. Fatigue behavior. unclear. To make fatigue behavior clear.

I am the owner, or an agent authorized to act on behalf of the owner, of the copyrighted work described.

Download Presentation

Fatigue Characteristic of RC Beams Strengthen with CFRP Strand sheet

An Image/Link below is provided (as is) to download presentation

Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author.While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server.


- - - - - - - - - - - - - - - - - - - - - - - - - - E N D - - - - - - - - - - - - - - - - - - - - - - - - - -

Presentation Transcript


Fatigue characteristic of rc beams strengthen with cfrp strand sheet

Fatigue Characteristic of RC Beams Strengthen with CFRP Strand sheet

B4 Junpei Kasai


Today s topic

Today’s Topic

・Background & Purpose

・Experiment & Result

・Future plan


Background purpose

Static behavior

Background & Purpose

clear

Fatigue behavior

unclear

To make fatigue behavior clear

To analyze residual strength after 2milion fatigue load


Experiment result

Experiment & Result

Maximum load 90kN

Minimum load10kN

・Specimen


Experiment result1

Experiment & Result

Figure of Crack


Experiment result2

Experiment & Result

Figure of Crack


Experiment result3

Experiment & Result

・Failure model

1layer Bending failure

Maximum load 250kN

Debonding occur at end of sheet

2layer Bending failure

Maximum load 260kN

Debonding occur at end of sheet


Experiment result4

Experiment & Result

Load-displacement at loading point of 1 layer


Experiment result5

Experiment & Result

Load-displacement at loading point of 1 2ayer


Experiment result6

Experiment & Result

Maximum load

Static After fatigue

1layer 278kN 250kN

2layers 315kN 260kN

Enough residual strength


Experiment result7

Experiment & Result

Strain of sheet


Experiment result8

Experiment & Result

Strain of sheet

The number of loads increase

Strain of sheet increase

Strain of sheet

1layer>2layer


Experiment result9

Experiment & Result

Bond stress of sheet


Experiment result10

Bond stress of sheet

1layer>2layers

Sheet debonding

Bond stress move

Experiment & Result


Future plan

~ 2009Dec24

Statictest

2009 Dec 25 ~

Analysis & Thesis

Future plan

Thank you for your kind attention !!